ABS 720FS
0
مقایسهبرگه داده فنی
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.05 g/cm | |
| melt mass-flow rate | 200℃×5kg | ASTM D-1238 | 3.0 g/10min |
| Shrinkage rate | 23℃ | ASTM D-955 | 0.5～0.7 % |
| melt mass-flow rate | 220℃×10kg | ASTM D-1238 | 30 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | 23℃ | ASTM D-785 | 105 R |
| elongation at break | 23℃ | ASTM D-638 | 35 % |
| Impact strength of cantilever beam gap | 23℃ 3.2mm | ASTM D-256 | 24 kg.cm/cm |
| bending strength | 23℃ | ASTM D-790 | 700 kg/cm |
| Flexural modulus | 23℃ | ASTM D-790 | 23000 kg/cm |
| tensile strength | 23℃ | ASTM D-638 | 500 kg/cm |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| coefficient of friction | 动态 | 与普通ABS对磨 | 0.14 |
| wear resistance | 15.2m/min,0.7kpa | 0.018 mm/h |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 6.4mm、1.82MPa，HDT | ASTM D-648 | 90 ℃ |