Cellulose, Regenerated XS440 Innovia Films Ltd.
0
- کاربردها:Filmpackagingtapefood packaging
مقایسهبرگه داده فنی
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 45°,30.6µm | ASTM D2457 | 105 |
| Haze ratio | 30.6µm | ASTM D1003 | 4.0 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.20 |
| Itself - Static | ASTM D1894 | 0.25 |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Secant modulus | 1%正割,MD:31µm | ASTM D882 | >3000 MPa |
| 1%正割,TD:31µm | ASTM D882 | >1500 MPa | |
| tensile strength | MD:屈服,31µm | ASTM D882 | 125 MPa |
| TD:屈服,31µm | ASTM D882 | 70.0 MPa | |
| elongation | MD:断裂,31µm | ASTM D882 | 22 % |
| TD:断裂,31µm | ASTM D882 | 70 % | |
| Sealing emphasis | 内部方法 | 2.2 N/mm | |
| Initial sealing temperature | 31µm | 内部方法 | 100to160 °C |
| oxygen permeability | 23°C,31µm,0.0%RH，湿 | ASTMF1927 | 3.00 cm³/m²/24hr |
| Water Vapor Transmission Rate | ASTME96 | 10 g/m²/24hr | |
| film thickness | 内部方法 | 30.6 µm | |
| usage | 30.6µm | 内部方法 | 22.7 m²/kg |