برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 260°C/2.16kg | cm³/10min | 0.05to0.07 |
| balance | | % | 0.055-0.21 |
| lateral flow | | mm/mm | 188.0E-3-208.3E-3 |
| flow | | mm/mm | 86.4E-3-0.330 |
| saturation | | % | 0.30-0.40 |
| Viscosity value | 23℃ | ml/g | 80.0-95.0 |
| Apparent density | | g/cm³ | 0.70-0.80 |
| melt mass-flow rate | 265°C/2.16kg | g/10min | 17to22 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | 23℃ | | 110to120 |
| ball-indentation hardness | | | 110.34to251.72 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Burning wire flammability index | | °C | 648to960 |
| Limiting Oxygen Index | | % | 21 |
| burning rate | | mm/min | 0.0to99.06 |
| Hot filament ignition temperature | | °C | 643to960 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| fracture | | % | 1.7-3.9 |
| yield | | % | 1.0-4.5 |
| fracture | | | 97.24to160.0 Mpa |
| yield | | | 163.45to172.41 Mpa |
| yield | | | 87.59to175.17 Mpa |
| yield | | % | 1.0-3.0 |
| fracture | | | 50.0to140.69 Mpa |
| yield | | | 89.66to140.69 Mpa |
| fracture | | % | 1.5-3.2 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 5.572to15.323 |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 1.067to2.229 |
| Dart impact | 23℃ | N.m | 469.91to626.55 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | ohms | 1.0E+14-1.1E+15 |
| Volume resistivity | 23℃ | ohms·cm | 1.0E+12-1.0E+16 |
| relative permittivity | 23℃ | | 3.76 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 2 |
| Dissipation Factor | 23℃ | | 8.0E-4-0.017 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| horizontal | | mm/mm/°C | 83.8E-5-152.4E-5 |
| RTI Imp | | °C | 75to125 |
| flow | | mm/mm/°C | 27.9E-5-50.8E-5 |
| flow | | mm/mm/°C | 30.5E-5-50.8E-5 |
| thermal conductivity | 23℃ | W/m2k | 0.30to0.33 |
| horizontal | | mm/mm/°C | 76.2E-5-101.6E-5 |
| RTI | | °C | 75to140 |
| RTI Elec | | °C | 75to140 |
| melting temperature | | °C | 237to240 |