PC+AS T88 GF-20 Covestro - Polycarbonates

ویژگی‌ها:
Filler glass fiber reinforced material 20% filler by weight
مقایسه

برگه داده فنی

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	23°C	ISO 527-2	120 MPa
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.00 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.00 kJ/m²
Tensile modulus	23°C	ISO 527-2	7200 MPa
Elongation at Break	23°C	ISO 527-2	2.40 %

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	TD	ISO 11359-2	6.5E-05 cm/cm／°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	3E-05 cm/cm／°C
Vicat softening temperature		ISO 306/B50	128 °C
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	119 °C
Hot deformation temperature	Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	129 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	(23°C,50RH)	ISO 62	0.20 %
Water absorption rate	Water absorption rate	(23°C,24hr)	ISO 62	0.40 %
Shrinkage rate	TD2.0mm	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	MD2.0mm	ISO 294-4	0.40 %
density		ISO 1183	1.29 g/cm³

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dissipation factor	23°C	IEC 60250	8.5E-03 1MHz
Dielectric constant	23°C	IEC 60250	3.20 1MHz
Dielectric strength		IEC 60243-1	35 KV/mm
Surface resistivity		IEC 60093	1E+17 Ω.cm
Volume resistivity		IEC 60093	1E+16 Ω.cm
Dissipation factor	相对漏电起痕指数	IEC 60112	150 V

flame retardant performance	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating		UL -94	HB 0.85mm