PPS Generic PPS - GlassMineral Generic
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | -- | ASTM D792 | 1.79to2.00 g/cm³ |
| 23°C | ISO 1183 | 1.81to2.00 g/cm³ | |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.15to0.31 % |
| TD:23°C | ASTM D955 | 0.38to1.0 % | |
| 23°C | ISO 294-4 | 0.14to0.70 % | |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.020to0.025 % |
| 23°C,24hr | ISO 62 | 0.019to0.020 % | |
| 饱和,23°C | ISO 62 | 0.020 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | 23°C | ASTM D785 | 99to122 |
| 23°C | ISO 2039-2 | 97to124 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 5.3to31 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 38to100 J/m |
| 23°C | ISO 180 | 5.9to7.0 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 200to320 J/m |
| 23°C | ISO 180 | 20 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.9to9.1 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | 23°C | ASTM D638 | 14200to19100 MPa |
| 23°C | ISO 527-2 | 10600to23000 MPa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 129to173 MPa |
| 断裂,23°C | ASTM D638 | 110to165 MPa | |
| 断裂,23°C | ISO 527-2 | 50.0to167 MPa | |
| 23°C | ASTM D638 | 100to174 MPa | |
| 23°C | ISO 527-2 | 113to172 MPa | |
| elongation | 断裂,23°C | ASTM D638 | 0.50to2.1 % |
| 断裂,23°C | ISO 527-2 | 0.43to1.8 % | |
| Flexural modulus | 23°C | ASTM D790 | 12800to20100 MPa |
| 23°C | ISO 178 | 10700to22100 MPa | |
| bending strength | 23°C | ASTM D790 | 172to261 MPa |
| 23°C | ISO 178 | 126to262 MPa | |
| compressive strength | 23°C | ASTM D695 | 138to295 MPa |
| shear strength | 23°C | ASTM D732 | 60.0to65.6 MPa |
| Poisson's ratio | 23°C | ASTME132 | 0.34to0.36 |
| coefficient of friction | ASTM D1894 | 0.30to0.35 | |
| Taber abraser | 23°C | ASTM D1044 | 70.0to70.8 mg |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| arc resistance | ASTM D495 | 180to186 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Surface Resistivity | ASTM D257 | 3.0E+3到1.0E+16 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 5.5E+2到2.5E+16 ohms·cm |
| 23°C | IEC 60093 | 1.0E+2到1.3E+16 ohms·cm | |
| dielectric strength | 23°C | ASTM D149 | 11to18 kV/mm |
| 23°C | IEC 60243-1 | 13to26 kV/mm | |
| dielectric constant | 23°C | ASTM D150 | 3.78to5.04 |
| 23°C | IEC 60250 | 3.97to5.85 | |
| 23°C | IEC 60250 | 5.15 | |
| Dissipation Factor | 23°C | ASTM D150 | 8.0E-4到9.2E-3 |
| 23°C | IEC 60250 | 1.0E-3到2.1E-3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9.6E-6到2.4E-5 cm/cm/°C |
| TD | ASTM D696 | 1.7E-5到4.8E-5 cm/cm/°C | |
| TD | ASTME831 | 3.0E-5到7.0E-5 cm/cm/°C | |
| TD | ISO 11359-2 | 1.9E-5到3.3E-5 cm/cm/°C | |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 215to220 °C |
| melting temperature | ISO 11357-3 | 278to280 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 4.0E-6到2.0E-5 cm/cm/°C |
| MD | ASTME831 | 1.0E-5到1.5E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 259to270 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 259to276 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.