برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 5.0to10 g/10min |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.50to0.70 % |
| density | | ASTM D792 | 1.21 g/cm³ |
| Shrinkage rate | TD：3.18mm | ASTM D955 | 0.50to0.70 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | 2540µm | ASTM D1003 | 85.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服,3.17mm | ASTM D638 | 62.1 MPa |
| tensile strength | Break,3.18mm | ASTM D638 | 55.2 MPa |
| elongation | 屈服,3.18mm | ASTM D638 | 7.0 % |
| elongation | 断裂,3.18mm | ASTM D638 | 90 % |
| Flexural modulus | 3.17mm | ASTM D790 | 2210 MPa |
| bending strength | 3.18mm | ASTM D790 | 89.6 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 640 J/m |
| Dart impact | 3.18mm | ASTM D3029 | >36.2 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| arc resistance | 1.50mm | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | 1.50mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 2 |
| High Voltage Arc Traceability Rate (HVTR) | 1.50mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 1 |
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | 1.50mm | ASTM D149 | 25 kV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI Imp | 1.5mm | UL 746 | 110 °C |
| RTI Imp | 3.0mm | UL 746 | 110 °C |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| RTI Str | 3.0mm | UL 746 | 125 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 135 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 129 °C |
| vicat | | ASTM D15252 | 149 °C |
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| RTI Elec | 3.0mm | UL 746 | 125 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.