optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Refractive index		ISO 489	1.573
transmissivity	1000μm	ISO 13468-2	89.0	%
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.5mm	UL 94	HB
Burning wire flammability index		IEC 60695-2-12	850	°C
Extreme Oxygen Index		ISO 4589-2	26	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Yield,23°C	ISO 527-2/50	6.6	%
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50	%
Bending modulus	23°C	ISO 178	2450	Mpa
bending strength	23°C	ISO 178	108	Mpa
Tensile modulus	23°C	ISO 527-2/1	2450	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	74.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	172	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	157	°C
Vicat softening temperature		ISO 306/B120	182	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
RTI Elec		UL 746	150	°C
RTI Imp		UL 746	130	°C
RTI Str		UL 746	150	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density	23°C	ISO 1183	1.15	g/cm³
melt mass-flow rate	330°C/2.16kg	ISO 1133	19	g/10min
Melt Volume Flow Rate (MVR)	330°C/2.16kg	ISO 1133	18.0	cm3/10min
Shrinkage rate	TD:2.00mm	ISO 294-4	0.85	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	0.85	%
Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dissipation factor	23°C,100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 4
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity	23°C	IEC 60093	1E+17	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	35	KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	2.90
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	2.80
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	127	Mpa
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Electrolytic corrosion	23°C	IEC 60426	A1