برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | 23°C | ISO 1183 | 1.03 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 3.0 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 28.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.40to0.70 % |
| density | --3 | ASTM D792 | 1.03 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.8mm | UL 94 | HB |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 30 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 320 J/m |
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 260 J/m |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 28 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 14 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服4 | ASTM D638 | 40.6 MPa |
| tensile strength | Yield | ISO 527-2/50 | 40.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 29.0 MPa |
| Flexural modulus | --6 | ISO 178 | 1800 MPa |
| bending strength | --5 | ASTM D790 | 63.4 MPa |
| bending strength | --6 | ISO 178 | 60.0 MPa |
| elongation | 断裂4 | ASTM D638 | 30 % |
| elongation | Break | ISO 527-2/50 | 30 % |
| Flexural modulus | --5 | ASTM D790 | 2140 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 82.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 95.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 96.0 °C |
| vicat | -- | ASTM D15257 | 105 °C |
| vicat | -- | ISO 306/A50 | 103 °C |
| vicat | -- | ISO 306/B50 | 94.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9.2E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.