برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Specific volume | | ASTM D792 | 0.830 cm³/g |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 2.0 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 2.00 cm³/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.80to1.0 % |
| saturation | | ISO 62 | 0.16 % |
| balance | | ISO 62 | 0.35 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 127 |
| Rockwell hardness | M-Scale | ASTM D785 | 92 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ASTM D542 | 1.600 |
| transmissivity | 2540µm | ASTM D1003 | 85.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.47mm | UL 94 | HB |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 74.0 J |
| Dart impact | 23°C | ASTM D3029 | 149 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 578 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.0 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| yield | | ASTM D638 | 65.5 MPa |
| yield | | ISO 527-2/50 | 68.0 MPa |
| fracture | | ASTM D638 | 77.9 MPa |
| yield | | ASTM D790 | 97.2 MPa |
| fracture | | ISO 527-2/50 | 68.0 MPa |
| yield | | ASTM D638 | 8.0 % |
| yield | | ISO 527-2/50 | 7.0 % |
| fracture | | ASTM D638 | 78 % |
| fracture | | ISO 527-2/50 | 100 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | 3.20mm,inAir | ASTM D149 | 20 kV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.27 |
| Dissipation Factor | 60Hz | ASTM D150 | 1.6E-03 |
| Dissipation Factor | 100Hz | ASTM D150 | 0.026 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| dielectric constant | 60Hz | ASTM D150 | 3.27 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric constant | 1MHz | ASTM D150 | 3.10 |
| Dissipation Factor | 50Hz | ASTM D150 | 1.6E-03 |
| Volume resistivity | | ASTM D257 | >2.5E+17 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1260 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.21 W/m/K |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI | | UL 746 | 130 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه