PVOH MonoSol® AF L711 Blue 50µ MonoSol, LLC
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| water content | 23°C | 7.4 wt% | |
| solubility | Disintegration:10°C,50.8µm | 27.0 sec | |
| Disintegration:24°C,50.8µm | 10.0 sec | ||
| Dissolution:10°C,50.8µm | 155.0 sec | ||
| Dissolution:24°C,50.8µm | 93.0 sec |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| usage | 50.0µm | ASTM D4321 | 15.6 m²/kg |
| Secant modulus | 100%,TD:51µm | ASTMD882 | 19.3 MPa |
| tensile strength | MD:断裂,51µm | ASTM D882 | 33.8 MPa |
| TD:断裂,51µm | ASTM D882 | 45.5 MPa | |
| MD:51µm | ISO 527-3 | 33.8 MPa | |
| TD:51µm | ISO 527-3 | 45.5 MPa | |
| elongation | MD:断裂,51µm | ASTMD882 | 290 % |
| TD:断裂,51µm | ASTMD882 | 280 % | |
| Dart impact | 51µm | ASTMD1709 | 960 g |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 1300 g |
| Secant modulus | 10%,TD:51µm | ASTMD882 | 73.8 MPa |
| Elmendorf tear strength | MD:51µm | ISO 6383-2 | 0.13 N |
| TD:51µm | ISO 6383-2 | 0.13 N | |
| film thickness | 50 µm | ||
| 20µmto60µm | |||
| Secant modulus | 10%,MD:51µm | ASTMD882 | 68.3 MPa |
| 100%,MD:51µm | ASTMD882 | 17.9 MPa | |
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 1300 g |