PA66 Vydyne® R535J NT0665
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.41 g/cm³ |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.90 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.6 % |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.40 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.80 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 775 °C |
| 1.5mm | IEC 60695-2-13 | 725 °C | |
| 3.0mm | IEC 60695-2-13 | 750 °C | |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 3.0mm | UL 94 | HB | |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 750 °C |
| 1.5mm | IEC 60695-2-12 | 725 °C | |
| 3.0mm | IEC 60695-2-12 | 800 °C |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Automotive Materials | thicknessd=1mm | FMVSS302 | + |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 11600 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 209 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.8 % |
| Flexural modulus | 23°C | ISO 178 | 10500 MPa |
| bending strength | 23°C | ISO 178 | 300 MPa |
| Poisson's Ratio | 23°C | ISO 527 | 0.40 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| 23°C | ISO 179/1eA | 12 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 68 kJ/m² |
| 23°C | ISO 179/1eU | 79 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 11 kJ/m² |
| 23°C | ISO 180 | 12 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | 0.750mm | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | 1.00mm | IEC 60243 | 20 kV/mm |
| High arc combustion index (HAI) | 0.75mm | UL 746 | PLC 0 |
| 1.5mm | UL 746 | PLC 0 | |
| 3.0mm | UL 746 | PLC 0 | |
| arc resistance | 3.00mm | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 4 |
| 1.5mm | UL 746 | PLC 4 | |
| 3.0mm | UL 746 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 260 °C | |
| 线性热膨胀系数 | MD：23到55°C | ISO 11359-2 | 2.1E-05 cm/cm/°C |
| TD：23to55°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| RTI Elec | 0.75mm | UL 746 | 120 °C |
| 1.5mm | UL 746 | 120 °C | |
| 3.0mm | UL 746 | 120 °C | |
| RTI Imp | 0.75mm | UL 746 | 100 °C |
| 1.5mm | UL 746 | 100 °C | |
| 3.0mm | UL 746 | 105 °C | |
| RTI Str | 0.75mm | UL 746 | 125 °C |
| 1.5mm | UL 746 | 125 °C | |
| 3.0mm | UL 746 | 125 °C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 261 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 251 °C |