برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmittance | 3.2mm | ASTM D-1003 | MF｜93 % |
| transmittance | 3.2mm | ASTM D-1003 | 93 % |
| refractive index | | ASTM D-542 | MF｜1.49 |
| refractive index | | ASTM D-542 | 1.49 |
| processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | | ASTM D-955 | MF｜0.2-0.6 % |
| Shrinkage rate | | ASTM D-955 | 0.2-0.6 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 24hr | ASTM D-570 | MF｜0.3 % |
| Water absorption rate | 24hr | ASTM D-570 | 0.3 % |
| melt mass-flow rate | 230℃,3.8kg | ASTM D-1238 | MF｜2.0 g/10min |
| melt mass-flow rate | 230℃,3.8kg | ASTM D-1238 | 2.5 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | | ASTM D-785 | MF｜100 M Scale |
| Rockwell hardness | | ASTM D-785 | 95 M Scale |
| elongation at break | | ASTM D-638 | MF｜5 % |
| elongation at break | | ASTM D-638 | 5 % |
| Impact strength of cantilever beam gap | 1/4″付 | ASTM D-255 | MF｜1.7 kg·cm/cm |
| Impact strength of cantilever beam gap | 1/4″付 | ASTM D-255 | 1.6 kg·cm/cm |
| tensile strength | | ASTM D-638 | MF｜740 kg/cm2 |
| tensile strength | | ASTM D-638 | 730 kg/cm2 |
| compressive strength | | ASTM D-695 | MF｜1100 kg/cm2 |
| compressive strength | | ASTM D-695 | 1100 kg/cm2 |
| Flexural modulus | 1/4″棒 | ASTM D-790 | MF｜3.2×104 kg/cm2 |
| Flexural modulus | 1/4″棒 | ASTM D-790 | 3.1×104 kg/cm2 |
| bending strength | 1/4″棒 | ASTM D-790 | MF｜1100 kg/cm2 |
| bending strength | 1/4″棒 | ASTM D-790 | 1100 kg/cm2 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric constant | 60Hz | | 3.7 |
| Volume resistivity | | JIS K-6911 | MF｜>1016 |
| Volume resistivity | | JIS K-6911 | >1016 |
| Dielectric loss | 60Hz，正切 | | MF｜0.05 |
| Dielectric loss | 60Hz，正切 | | 0.05 |
| Volume resistivity | | JIS K-6911 | MF｜>1015 |
| Volume resistivity | | JIS K-6911 | >1015 |
| arc resistance | | JIS K-6911 | MF｜没有痕迹 |
| arc resistance | | JIS K-6911 | 没有痕迹 |
| dielectric strength | | | MF｜20 |
| dielectric strength | | | 20 |
| dielectric constant | 60Hz | | MF｜3.7 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | 1kg | ASTM D-1525 | MF｜116 °C |
| vicat | 1kg | ASTM D-1525 | 107 °C |
| thermal conductivity | | ASTM C-177 | MF｜5×10-4 Cal/s/cm/℃ |
| thermal conductivity | | ASTM C-177 | 5×10-4 Cal/s/cm/℃ |
| specific heat | | | MF｜0.35 cal/g/℃ |
| specific heat | | | 0.35 cal/g/℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | MF｜6×10-5 cm/cm/℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | 6×10-5 cm/cm/℃ |
| Heat distortion temperature | 18.56kg/cm2 | ASTM D-648 | MF｜102 °C |
| Heat distortion temperature | 18.56kg/cm2 | ASTM D-648 | 92 °C |