برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.29 g/cm³ |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 10 g/10min |
| melt mass-flow rate | 265°C/5.0kg | ASTM D1238 | 13 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.60to0.95 % |
| Shrinkage rate | TD | ASTM D955 | 0.50to0.70 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R级,3.20mm,注塑 | ASTM D785 | 110 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| UL flame retardant rating | 2.0mm | UL 94 | V-0 |
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 825 °C |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | 2.5mm | IEC 60695-2-12 | 960 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 3.20mm,注塑 | ASTM D638 | 2330 MPa |
| tensile strength | 屈服,3.20mm,注塑 | ASTM D638 | 53.0 MPa |
| tensile strength | 断裂,3.20mm,注塑 | ASTM D638 | 45.0 MPa |
| elongation | 屈服,3.20mm,注塑 | ASTM D638 | 4.1 % |
| elongation | 断裂,3.20mm,注塑 | ASTM D638 | 150 % |
| Flexural modulus | 3.20mm,注塑 | ASTM D790 | 2270 MPa |
| bending strength | 3.20mm,注塑 | ASTM D790 | 82.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm,注塑 | ASTM D256 | 750 J/m |
| Dart impact | 0°C,3.20mm,注塑,PeakEnergy | ASTM D3763 | 49.0 J |
| Dart impact | 0°C,3.20mm,注塑,TotalEnergy | ASTM D3763 | 62.0 J |
| Dart impact | 23°C,3.20mm,注塑,PeakEnergy | ASTM D3763 | 45.0 J |
| Dart impact | 23°C,3.20mm,注塑,总能量 | ASTM D3763 | 60.0 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 5.2E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+18 ohms·cm |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 31 kV/mm |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 18 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 3.28 |
| relative permittivity | 1MHz | IEC 60250 | 3.12 |
| Dissipation Factor | 100Hz | IEC 60250 | 3E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 79.0 °C |
| vicat | | ASTM D15256 | 140 °C |
| Linear coefficient of thermal expansion | MD：-40到80°C | ASTM D696 | 7.4E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 109 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.