PA6 Starflam BFR552Y3 EUROSTAR FRANCE

ویژگی‌ها:

Filler glass mineral

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

ویژگی‌ها:

Filler | glass mineral

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	2.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	25	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	30	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	3.0	kJ/m²
	Impact strength of cantilever beam gap	-20°C	ISO 180/1A	3.0	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.75mm	UL 94	V-2
Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	24	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Break	ISO 527-2/5	85.0	MPa
Tensile strain	Break	ISO 527-2/5	2.8	%
Bending modulus		ISO 178	5500	MPa
bending strength		ISO 178	145	MPa
Tensile modulus		ISO 527-2/1	5800	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	4.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7E-05	cm/cm/°C
RTI Elec		UL 746	65.0	°C
RTI Imp		UL 746	65.0	°C
RTI		UL 746	65.0	°C
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	210	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	180	°C
Vicat softening temperature	--	ISO 306/B50	205	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	207	°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183	1.34	g/cm³
Shrinkage rate	MD	Internal Method	0.40to0.60	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	kV/mm
Relative permittivity	50Hz	IEC 60250	3.40
	Relative permittivity	60Hz	IEC 60250	3.40
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.30
Dissipation factor	50Hz	IEC 60250	5.7E-03
	Dissipation factor	60Hz	IEC 60250	5.7E-03
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.014
Compared to the anti leakage trace index		IEC 60112	PLC 1
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	L-Sale	ISO 2039-2	110