| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183/B | 1.20 g/cm³ |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 15 g/10min |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | | ASTM D1003 | 87.0to91.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 800 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 800 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 34 % |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| UL flame retardant rating | 2.5mm | UL 94 | V-0 |
| Burning wire flammability index | 1.0mm3 | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | 2.0mm4 | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | 3.0mm4 | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 800 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 2400 MPa |
| tensile strength | Yield | ISO 527-2 | 60.0 MPa |
| tensile strength | Break | ISO 527-2 | 70.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 6.0 % |
| Tensile strain | Break | ISO 527-2 | 110 % |
| Flexural modulus | | ISO 178 | 2350 MPa |
| bending strength | | ISO 178 | 95.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 65 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 1Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 17 kV/mm |
| dielectric constant | 1Hz | IEC 60250 | 2.70 |
| dielectric constant | 50Hz | IEC 60250 | 2.70 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 143 °C |
| Ball pressure temperature | | IEC 60335-1 | >125 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 124 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 140 °C |
| vicat | | ISO 306/B50 | 148 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.