POM Copolymer Ultraform® N 2650 Z4 BASF GERMANY

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	15 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	270 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield,23°C	ISO 527-2	45.0 MPa
Tensile strain	Yield,23°C	ISO 527-2	16 %
Nominal tensile fracture strain	23°C	ISO 527-2	40 %
Tensile creep modulus	1000hr	ISO 899-1	500 MPa
Tensile modulus	23°C	ISO 527-2	1500 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Melting temperature		ISO 3146	167 °C
Linear coefficient of thermal expansion	MD		1.3E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.35 g/cm³
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	7.00 cm³/10min

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	1E+13 ohms·cm
Dielectric constant	1MHz	IEC 60250	4.20
Dissipation factor	1MHz	IEC 60250	0.017
Compared to the anti leakage trace index		IEC 60112	PLC 0