impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	40	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	9.0	kJ/m²
	Impact strength of cantilever beam gap	0°C	ISO 180/1A	15	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	45	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Dart impact	-20°C,TotalEnergy	ASTM D3763	70.0	J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	70.0	J
Multi axis Instrumented Impact Energy		ISO 6603-2	110	J
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Yield	ISO 527-2/50	4.2	%
elongation	Break3	ASTM D638	150	%
elongation	elongation	Break4	ASTM D638	140	%
Tensile strain	Break	ISO 527-2/5	120	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	110	%
Bending modulus	50.0mmSpan	ASTM D790	3100	Mpa
Bending modulus	Bending modulus		ISO 178	2900	Mpa
bending strength		ISO 178	90.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	96.0	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	30.0	mg
tensile strength	Yield	ASTM D638	60.0	Mpa
	tensile strength	Yield	ISO 527-2/5	55.0	Mpa
		tensile strength	Yield	ISO 527-2/50	61.0	Mpa
			tensile strength	Break3	ASTM D638	60.0	Mpa
				tensile strength	Break4	ASTM D638	60.0	Mpa
					tensile strength	Break	ISO 527-2/5	60.0	Mpa
					tensile strength	tensile strength	Break	ISO 527-2/50	55.0	Mpa
elongation	Yield	ASTM D638	4.5	%
elongation	elongation	Yield	ASTM D638	4.1	%
Tensile strain	Yield	ISO 527-2/5	4.1	%
Tensile modulus		ASTM D638	3400	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3200	Mpa
tensile strength	Yield	ASTM D638	56.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	125	°C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	119	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	106	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	97.0	°C
Vicat softening temperature		ASTM D152511	133	°C
	Vicat softening temperature	--	ISO 306/B50	133	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	135	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-30to80°C	ISO 11359-2	7.2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8.2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to80°C	ISO 11359-2	9E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	266°C/5.0kg	ASTM D1238	7.0	g/10min
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	6.00	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.70-0.90	%
Water absorption rate	Saturation,23°C	ISO 62	0.42	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.14	%
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test	H358/30	ISO 2039-1	105	Mpa