PA66 Vydyne® R515H BK02

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.24 g/cm³
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.50 %
Water absorption rate	23°C,24hr	ISO 62	1.0 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	2.2 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	0.75mm	IEC 60695-2-12	675 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	675 °C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	675 °C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	700 °C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	700 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	700 °C

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength	23°C	ISO 178	170 MPa
Tensile modulus	23°C	ISO 527-2	6600 MPa
tensile strength	断裂,23°C	ISO 527-2	120 MPa
Tensile strain	断裂,23°C	ISO 527-2	3.0 %
Flexural modulus	23°C	ISO 178	5900 MPa
Poisson's ratio		ISO 527-2	0.40

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ISO 180	6.6 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	6.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	32 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	39 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180	5.7 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot wire ignition (HWI)	0.75mm	UL 746	PLC 4
	Hot wire ignition (HWI)	1.5mm	UL 746	PLC 3
	Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0mm	UL 746	PLC 4
High arc combustion index (HAI)	0.75mm	UL 746	PLC 0
	High arc combustion index (HAI)	1.5mm	UL 746	PLC 0
	High arc combustion index (HAI)	High arc combustion index (HAI)	3.0mm	UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)	HVTR	UL 746	PLC 1
Volume resistivity	0.750mm	IEC 60093	1E+13 ohms·cm
dielectric strength	1.00mm	IEC 60243	20 kV/mm
arc resistance	3.00mm	ASTM D495	PLC6
Compared to the Leakage Tracking Index (CTI)	3.00mm	IEC 60112	PLC 2

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
RTI Imp	1.5mm	UL 746	120 °C
RTI Imp	RTI Imp	3.0mm	UL 746	120 °C
RTI Str	0.75mm	UL 746	125 °C
Hot deformation temperature (HDT)	0.45MPa,未退火，HDT	ISO 75-2/B	258 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)	1.8MPa,未退火，HDT	ISO 75-2/A	241 °C
melting temperature		ISO 11357-3	260 °C
线性热膨胀系数	MD：23to55°C,2.00mm	ISO 11359-2	3E-05 cm/cm/°C
线性热膨胀系数	线性热膨胀系数	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C
RTI Elec	0.75mm	UL 746	140 °C
RTI Elec	RTI Elec	1.5mm	UL 746	140 °C
RTI Str	1.5mm	UL 746	140 °C
RTI Str	RTI Str	3.0mm	UL 746	140 °C
RTI Elec	3.0mm	UL 746	140 °C
RTI Imp	0.75mm	UL 746	120 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.