| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Specific volume | | ASTM D792 | 0.660 cm³/g |
| Shrinkage rate | 流动 : 1.50 到 3.20 mm | 内部方法 | 0.30 - 0.50 % |
| Shrinkage rate | 流动 : 3.20 到 4.60 mm | 内部方法 | 0.50 - 0.80 % |
| Shrinkage rate | 横向流动 : 1.50 到 3.20 mm | 内部方法 | 0.40 - 0.60 % |
| Shrinkage rate | 横向流动 : 3.20 到 4.60 mm | 内部方法 | 0.60 - 0.90 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 % |
| Outdoor applicability | | UL 746C | f2 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R 级 | ASTM D785 | 119 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 断裂 | ASTM D638 | 110 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 6890 Mpa |
| bending strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 189 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 640 J/m |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 6.00 J |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 8.00 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 5.9E+16 ohms·cm |
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 29 KV/mm |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 24 KV/mm |
| dielectric constant | 100 Hz | ASTM D150 | 3.60 |
| dielectric constant | 1 MHz | ASTM D150 | 3.60 |
| Dissipation Factor | 100 Hz | ASTM D150 | 1.4E-3 |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.020 |
| arc resistance | | ASTM D495 | PLC 6 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| High arc combustion index (HAI) | | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | | UL 746 | PLC 1 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 3.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 to 80 % |
| Temperature at the rear of the barrel | | | 240 to 255 °C |
| Temperature in the middle of the barrel | | | 245 to 260 °C |
| Temperature at the front of the material cylinder | | | 250 to 265 °C |
| Spray nozzle temperature | | | 245 to 260 °C |
| Processing (melt) temperature | | | 250 to 265 °C |
| Temperature | | | 65 to 90 °C |
| Back pressure | | | 0.300 to 0.700 Mpa |
| screw speed | | | 50 to 80 rpm |
| Exhaust hole depth | | | 0.025 to 0.038 mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 215 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 176 °C |
| Linear coefficient of thermal expansion | -40 到 40°C，流动 | ASTM E831 | 2.3E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 60 到 138°C，流动 | ASTM E831 | 1.6E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 125 °C |
| RTI Imp | | UL 746 | 110 °C |
| RTI | | UL 746 | 125 °C |