| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | g/cm³ | 1.50 -- |
| Water absorption rate | 23°C,24hr | % | 0.18 -- |
| Water absorption rate | 饱和,23°C | % | 0.72 -- |
| Water absorption rate | 平衡,23°C,50%RH | % | 0.17 -- |
| Water absorption rate | 23°C,3.00mm2 | mg | 16.0 -- |
| Water absorption rate | 23°C,3.00mm3 | mg | 32.00.36 -- |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤,10.0mm | | 84 -- |
| ball-indentation hardness | 10.0mm | MPa | 140 -- |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.0mm | | HB -- |
| UL flame retardant rating | 6.0mm | | HB -- |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | -- | MPa | 55.0 -- |
| Tensile strain | Break | % | 10 10 |
| compression stress | 1%应变 | MPa | 26.0 -- |
| compression stress | 2%应变 | MPa | 44.0 -- |
| compression stress | 5%应变 | MPa | 77.0 -- |
| Tensile modulus | | MPa | 3100 3100 |
| tensile strength | Break | MPa | 55.0 55.0 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 3.0 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | 30 -- |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | ohms | >1.0E+13 >1.0E+13 |
| Volume resistivity | | ohms·cm | >1.0E+14 >1.0E+14 |
| dielectric strength | 1.00mm,在油中 | kV/mm | 20 20 |
| relative permittivity | 100Hz | | 3.60 3.60 |
| relative permittivity | 1MHz | | 3.60 3.60 |
| Dissipation Factor | 100Hz | | 3E-03 3E-03 |
| Dissipation Factor | 1MHz | | 8E-03 8E-03 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 100 -- |
| melting temperature | | °C | 180 -- |
| Linear coefficient of thermal expansion | MD：23到60°C | cm/cm/°C | 1.1E-04 -- |
| Linear coefficient of thermal expansion | MD：23到100°C | cm/cm/°C | 1.2E-04 -- |
| thermal conductivity | 23°C | W/m/K | 0.31 -- |
| Minimum operating temperature | | °C | -20 -- |
| maximum service temperature | continuously:for20,000h | °C | 90 -- |
| maximum service temperature | continuously:for5,000h | °C | 105 -- |
| maximum service temperature | forshortperiods | °C | 150 -- |