PP J-740

مقایسه

برگه داده فنی

Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate			优级品｜25 g/10min
	melt mass-flow rate			一级品｜25 g/10min
	melt mass-flow rate	melt mass-flow rate			合格品｜25 g/10min

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23℃		一级品｜≥80 J/M
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃		合格品｜≥80 J/M
tensile strength	屈服		优级品｜≥22 MPa
	tensile strength	屈服		一级品｜≥22 MPa
	tensile strength	tensile strength	屈服		合格品｜≥22 MPa
Flexural modulus			优级品｜≥1000 MPa
	Flexural modulus			一级品｜≥1000 MPa
	Flexural modulus	Flexural modulus			合格品｜≥1000 MPa
Impact strength of cantilever beam gap	23℃		优级品｜≥80 J/M

Other performance	شرایط آزمون	روش آزمون	نتیجه آزمون
cleanliness	色粒		优级品｜0-5 个/kg
	cleanliness	色粒		一级品｜6-10 个/kg
		cleanliness	色粒		合格品｜11-20 个/kg
		cleanliness	cleanliness	杂粒		合格品｜11-20 个/kg
ash content			优级品｜≤0.04 %
	ash content			一级品｜≤0.04 %
	ash content	ash content			合格品｜≤0.04 %
cleanliness	杂粒		优级品｜0-5 个/kg
cleanliness	cleanliness	杂粒		一级品｜6-10 个/kg

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat			优级品｜140 ℃
	vicat			一级品｜140 ℃
	vicat	vicat			合格品｜140 ℃