| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.15 g/cm³ |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 12 g/10min |
| Shrinkage rate | | 内部方法 | 0.55 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.10 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Limiting Oxygen Index | | ASTM D2863 | 23 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 0°C | ASTM D256 | 400 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 90 J/m |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 350 J/m |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| elongation | Break | ASTM D638 | 2.0 % |
| Flexural modulus | | ASTM D790 | 2350 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| vicat | | ASTM D15252 | 110 °C |
| ball-indentation hardness | 125°C | IEC 335 | 通过 |