| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.56 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.76 % |
| Shrinkage rate | MD | ISO 294-4 | 0.33 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 4.5 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.4 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 725 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile strain | Break | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 13000 MPa |
| bending strength | | ISO 178 | 310 MPa |
| Tensile modulus | | ISO 527-2 | 16500 MPa |
| tensile strength | Break | ISO 527-2 | 220 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 95 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| relative permittivity | 1MHz | IEC 60250 | 5.20 |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C |
| melting temperature | | ISO 11357-3 | 220 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 5E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.