PP LUBLENE GF30 NATURAL LUBEN PLAST srl

ویژگی‌ها:

Filler glass fiber reinforced material 30% filler by weight

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

ویژگی‌ها:

Filler | glass fiber reinforced material | 30% | filler by weight

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	30to40	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0-6.0	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	30to40	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/A	5.0-6.0	kJ/m²
	Impact strength of cantilever beam gap	23°C4	ASTM D256	5.0-6.0	kJ/m²
		Impact strength of cantilever beam gap	23°C3	ASTM D256	30to40	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256A	50to60	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0-6.0	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	30to40	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	30to40	kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256A	50to60	J/m
	Impact strength of cantilever beam gap	23°C3	ASTM D256	30to40	kJ/m²
		Impact strength of cantilever beam gap	23°C4	ASTM D256	5.0-6.0	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	5.0-6.0	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Break	ISO 527-2/1A/5	2.0to2.5	%
Tensile strain	Tensile strain	Yield	ISO 527-2/1A/5	2.0to2.5	%
tensile strength	Break	ISO 527-2/1A/5	70.0to80.0	MPa
tensile strength	tensile strength	Yield	ISO 527-2/1A/5	70.0to80.0	MPa
Tensile modulus		ISO 527-2/1A/1	5000to6000	MPa
Tensile strain	Break	ISO 527-2/1A/5	2.0to2.5	%
Tensile strain	Tensile strain	Yield	ISO 527-2/1A/5	2.0to2.5	%
tensile strength	Break	ISO 527-2/1A/5	70.0to80.0	MPa
tensile strength	tensile strength	Yield	ISO 527-2/1A/5	70.0to80.0	MPa
Tensile modulus		ISO 527-2/1A/1	5000to6000	MPa
Bending modulus		ISO 178	4500to5500	MPa
bending strength		ISO 178	80.0to90.0	MPa
Bending modulus		ISO 178	4500to5500	MPa
bending strength		ISO 178	80.0to90.0	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melting temperature		Internal Method	165to170	°C
Vicat softening temperature	--	ISO 306/B120	125to135	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A120	155to165	°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	130to140	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145to155	°C
		Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	145to155	°C
			Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145to155	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	130to140	°C
Vicat softening temperature	--	ISO 306/A120	155to165	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	125to135	°C
Melting temperature		Internal Method	165to170	°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	145to155	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183/A	1.10to1.14	g/cm³
density	density		ISO 1183/A	1.10to1.14	g/cm³