| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.85to1.95 g/cm³ |
| Apparent density | | ISO 60 | 0.60to0.80 g/cm³ |
| Shrinkage rate | MD2 | ISO 2577 | 0.30to0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.10 % |
| Shrinkage rate | | ISO 2577 | <0.050 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compression molding pressure | | | >20.0 MPa |
| Compression molding temperature | | | 165to180 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | Injection | ISO 178 | 18000to22000 MPa |
| bending strength | Compression Molded | ISO 178 | 150to180 MPa |
| bending strength | Injection | ISO 178 | 220to240 MPa |
| compression stress | | ISO 604 | 280to330 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 14000to18000 MPa |
| Tensile modulus | Injection | ISO 527-2 | 16000to20000 MPa |
| tensile strength | CompressionMolded | ISO 527-2 | 80.0to100 MPa |
| tensile strength | Injection | ISO 527-2 | 120to140 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 16000to18000 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 4.0to6.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 5.0to7.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 8.0to10 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 12to14 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+12到1.0E+13 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20to30 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 6.008.00 |
| relative permittivity | 1MHz | IEC 60250 | 4.006.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.10to0.20 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020to0.030 |
| arc resistance | | ASTM D495 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 160to180 °C |
| Linear coefficient of thermal expansion | MD：50到150°C | ISO 11359-2 | 1.5E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40to0.60 W/m/K |
| maximum service temperature | <50h | IEC 60216 | 230 °C |
| maximum service temperature | 20,000h | IEC 60216 | 150 °C |