Cellulose, Regenerated 430MS Innovia Films Ltd.

کاربردها:
Packaging film tape
مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
gloss	45°,29.9μm	ASTM D2457	90
turbidity	29.9μm	ASTM D1003	4.0 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Friction coefficient	Itself - Dynamic	ASTM D1894	0.20
Friction coefficient	Friction coefficient	Itself - Static	ASTM D1894	0.25

film	شرایط آزمون	روش آزمون	نتیجه آزمون
Secant modulus	1%Secant,MD:30μm	ASTM D882	>3000 MPa
Secant modulus	Secant modulus	1%Secant,TD:30μm	ASTM D882	>1500 MPa
tensile strength	MD:Yield,30μm	ASTM D882	125 MPa
tensile strength	tensile strength	TD:Yield,30μm	ASTM D882	70.0 MPa
elongation	MD:Break,30μm	ASTM D882	22 %
consumption	29.9μm	Internal Method	23.3 m²/kg
Initial sealing temperature	30μm	Internal Method	90.0to160 °C
elongation	TD:Break,30μm	ASTM D882	70 %
Sealing emphasis		Internal Method	1.8 N/mm
Oxygen permeability rate	23°C,30μm,0.0%RH，湿	ASTMF1927	3.00 cm³/m²/24hr
Water vapor permeability		ASTME96	20 g/m²/24hr
film thickness		Internal Method	29.9 µm