| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.04 g/cm | |
| Shrinkage rate | Flow | ASTM D-955 | 0.30-0.70 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 200℃,5kg | ASTM D-1238 | 3.5 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 断裂 | ASTM D-638 | 28.0 MPa |
| elongation at break | ASTM D-638 | 30 % | |
| Flexural modulus | ASTM D-790 | 2480 MPa | |
| bending strength | ASTM D-790 | 61.0 MPa | |
| Impact strength of cantilever beam gap | -18℃,3.20mm | ASTM D-256 | 59.0 J/m |
| 23℃,3.20mm | ASTM D-256 | 128 J/m | |
| Rockwell hardness | ASTM D-785 | 110 R scale | |
| Tensile modulus | ASTM D-638 | 2280 MPa | |
| tensile strength | 屈服 | ASTM D-638 | 29.0 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，未退火，HDT | ASTM D-648 | 89.0 ℃ |
| 1.80MPa，未退火，HDT | ASTM D-648 | 77.0 ℃ | |
| vicat | Rate B,120℃/h,Loading 1(10N) | ASTM D-1525 | 103 ℃ |
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000090 cm/cm℃ |
| combustibility | 1.47mm | UL 94 | HB |