PP Chiao Fu PP PP212GB20 NAT TAIWAN CHIAO FU
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.03 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 12 g/10min |
| Shrinkage rate | MD | ASTM D955 | <1.0 % |
| density | ASTM D792 | 1.03 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 12 g/10min |
| Shrinkage rate | MD | ASTM D955 | <1.0 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| bending strength | ASTM D790 | 53.9 MPa | |
| tensile strength | ASTM D638 | 31.4 MPa | |
| elongation | Break | ASTM D638 | <10 % |
| Flexural modulus | ASTM D790 | 1770 MPa | |
| tensile strength | ASTM D638 | 31.4 MPa | |
| elongation | Break | ASTM D638 | <10 % |
| Flexural modulus | ASTM D790 | 1770 MPa | |
| bending strength | ASTM D790 | 53.9 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 39 J/m | |
| ASTM D256 | 39 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 120 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 120 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.