flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating		UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength		ASTM D638	82.4	Mpa
elongation	Break	ASTM D638	30	%
Bending modulus		ASTM D790	2940	Mpa
bending strength		ASTM D790	118	Mpa
injection	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
drying temperature			80 to 100	°C
drying time			4.0 to 5.0	hr
Suggested maximum moisture content			< 0.20	%
Temperature at the rear of the barrel			270 to 280	°C
Temperature in the middle of the barrel			280 to 285	°C
Temperature at the front of the material cylinder			285 to 290	°C
Spray nozzle temperature			280 to 285	°C
Processing (melt) temperature			280 to 285	°C
Mold temperature			60 to 90	°C
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	230	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	85.0	°C
Melting temperature		DSC	260	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	Flow		1.8 - 2.0	%
Water absorption rate	24 hr, 23°C	ASTM D570	1.3	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		ASTM D257	1.0E+15	ohms·cm
Dielectric strength		ASTM D149	23	KV/mm
Dielectric constant	1 MHz	ASTM D150	3.20
Arc resistance		ASTM D495	190	sec
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Scale	ASTM D785	118