برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| viscosity number | | ISO 307 | 90.0 cm³/g |
| Shrinkage rate | free,longitudinal | | 0.10 % |
| Shrinkage rate | free,transverse | | 0.75 % |
| density | | ISO 1183 | 1.73 g/cm³ |
| Apparent density | | | 0.70to0.80 g/cm³ |
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 8.50 cm³/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.77 % |
| Shrinkage rate | MD | ISO 294-4 | 0.24 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flammability level | 0.75mm | IEC 60695-11-10,-20 | HB |
| Flammability level | 1.6mm | IEC 60695-11-10,-20 | HB |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 18000 MPa |
| tensile strength | Break | ISO 527-2 | 170 MPa |
| Tensile strain | Break | ISO 527-2 | 1.6 % |
| Flexural modulus | | ISO 178 | 17700 MPa |
| bending strength | | ISO 178 | 270 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| 相对电容率 | 100Hz | IEC 60250 | 4.70 |
| 相对电容率 | 1MHz | IEC 60250 | 4.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 221 °C |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |
| melting temperature | | ISO 11357-3 | 223 °C |
| 线性热膨胀系数 | MD：23到80°C | ISO 11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| specific heat | | | 950 J/kg/°C |
| Temperature index at | --4 | IEC 60216 | 140 °C |
| Temperature index at | 最高使用温度-shortcycleoperation | IEC 60216 | 210 °C |
| Temperature index at | --5 | IEC 60216 | 160 °C |