برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | 3.17 mm，Flow | ASTM D955 | 0.20 - 0.40 % |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.12 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R 级 | ASTM D785 | 120 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| UL flame retardant rating | 3.0 mm | UL 94 | V-0 |
| UL flame retardant rating | 2.4 mm | UL 94 | 5VA |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 875 °C |
| Limiting Oxygen Index | | ASTM D2863 | 37 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服, 3.17 mm | ASTM D638 | 62.0 Mpa |
| elongation | 断裂, 3.17 mm | ASTM D638 | 15 % |
| Flexural modulus | 3.17 mm | ASTM D790 | 3100 Mpa |
| bending strength | 屈服, 3.17 mm | ASTM D790 | 96.5 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 3.17 mm | ASTM D1822 | 53.3 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | --3 | ASTM D257 | 3.0E+15 ohms·cm |
| Volume resistivity | --4 | ASTM D257 | 6.0E+15 ohms·cm |
| dielectric strength | 3.00 mm | ASTM D149 | 19 KV/mm |
| arc resistance | | ASTM D495 | 0.00 to 120 sec |
| arc resistance | | ASTM D495 | PLC 7 PLC 6 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | V |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | mm/min |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | sec |
| Hot wire ignition (HWI) | | UL 746 | |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 138 °C |
| RTI Elec | | UL 746 | 80.0 to 125 °C |
| RTI Imp | | UL 746 | 80.0 to 115 °C |
| RTI | | UL 746 | 80.0 to 125 °C |