برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.30 % |
| density | | ISO 1183 | 1.04 g/cm³ |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 40 g/10min |
| density | | ASTM D792 | 1.05 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R级 | ASTM D785 | 114 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | | ASTM D790 | 73.0 Mpa |
| bending strength | | ISO 178 | 77.0 Mpa |
| Flexural modulus | | ASTM D790 | 2300 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2600 Mpa |
| tensile strength | 屈服 | ASTM D638 | 46.0 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 51.0 Mpa |
| elongation | 断裂 | ASTM D638 | 15 % |
| Tensile strain | 断裂 | ISO 527-2/50 | >10 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 0°C,3.20mm | ASTM D256 | 160 J/m |
| Impact strength of cantilever beam gap | 0°C,12.7mm | ASTM D256 | 110 J/m |
| Impact strength of cantilever beam gap | -30°C,12.7mm | ASTM D256 | 80 J/m |
| Impact strength of cantilever beam gap | -30°C,3.20mm | ASTM D256 | 110 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 18 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 220 J/m |
| Impact strength of cantilever beam gap | 23°C,12.7mm | ASTM D256 | 200 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | | ASTM D149 | 23 KV/mm |
| dielectric constant | 1kHz | ASTM D150 | 3.10 |
| Surface Resistivity | | ASTM D257 | >1.0E+16 ohms |
| Volume resistivity | 23°C | ASTM D257 | >1.0E+16 ohms·cm |
| Dissipation Factor | 1kHz | ASTM D150 | 6.2E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 81.0 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.2E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.16 W/m/K |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 92.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 86.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.