GPPS SDR 103 Schulman Plastics

ویژگی‌ها:
Flame retardant
good impact resistance
high heat resistance
مقایسه

برگه داده فنی

Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.06 g/cm
Melt volume flow rate	200℃,5kg	ISO 1133	12.0 cm

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile strain	屈服	ISO 527-1	2.5 %
Charpy Notched Impact Strength	-30℃	ISO 179/1eA	4.00 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179/1eA	8.00 KJ/m
Impact strength of simply supported beam without notch	-30℃	ISO 179/1eU	70.0 KJ/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	90.0 KJ/m
Tensile modulus		ISO 527-1	2300 MPa
Tensile stress	屈服	ISO 527-1	23.0 MPa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa，未退火，HDT	ISO 75B-1	84.0 ℃
Heat distortion temperature	Heat distortion temperature	1.80MPa，未退火，HDT	ISO 75A-1	76.0 ℃
vicat	A50(50N,50℃/h)	ISO 306	96.0 ℃
vicat	vicat	B50(50N,50℃/h)	ISO 306	89.0 ℃
combustibility	1.60mm	UL 94	V-2
Limiting Oxygen Index (LOI)		ISO 4589-1-2	23 %

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.