XLPE Pexidan® V/T USA Saco Polymers

مقایسه

برگه داده فنی

	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	UL 1581	11.0 MPa
	tensile strength	Break	UL 1581	12.8 MPa
		tensile strength	断裂2	UL 1581	11.7 MPa
			tensile strength	断裂3	UL 1581	12.7 MPa
			tensile strength	tensile strength	断裂4	UL 1581	12.1 MPa
elongation	Break	UL 1581	280 %
	elongation	断裂2	UL 1581	230 %
		elongation	断裂3	UL 1581	300 %
		elongation	elongation	断裂4	UL 1581	250 %
density		ASTM D792	1.30 g/cm³
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.80 g/10min
Degree of crosslinking		ASTM D2765	60 %
brittle temperature		ASTM D746	<-45.0 °C
deformation		UL 1581	1.0 %
relative permittivity	90°C	UL 1581	3.20
dielectric strength	--	UL 1581	21500 V
dielectric strength	dielectric strength	afterglancingimpact	UL 1581	18000 V
insulation resistance	23°C	UL 1581	34000 Mohms/1000ft
	insulation resistance	90°C	UL 1581	25000 Mohms/1000ft
	insulation resistance	insulation resistance	after12weeks:90°C	UL 1581	29000 Mohms/1000ft
Limiting Oxygen Index	4.00mm	ASTM D2863	27 %
CrushingTest		UL 1581	578330 g
HotElongation	150°C	内部方法	50 %