برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 3.00 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.20-0.40 % |
| ash content | | | 16 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 37.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.40-0.60 % |
| Shrinkage rate | MD | ISO 294-4 | 0.40-0.60 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 135 Mpa |
| ball-indentation hardness | | ISO 2039-1 | 110 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| burning rate | 2.00mm | ISO 3795 | 60 mm/min |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 700 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
| Flexural modulus | | ISO 178 | 5400 Mpa |
| bending strength | | ISO 178 | 101 Mpa |
| Tensile modulus | | ISO 527-2 | 5500 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 74.0 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 74.0 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 2500 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 44.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 2.1 % |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | >15 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 2200 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1500 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| bending strength | 23°C | ISO 178 | 70.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 20 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 18 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | 1.50mm | IEC 60243-1 | 32 KV/mm |
| relative permittivity | 100Hz | IEC 60250 | 2.90 |
| relative permittivity | 1MHz | IEC 60250 | 3.10 |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 6E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 34 KV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.00 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 2.90 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 5.5E-03 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 9E-03 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 106 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 102 °C |
| vicat | | ISO 306/B50 | 105 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-1 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 93.0 °C |
| vicat | | ISO 306/B50 | 98.0 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 97.0 °C |