optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
turbidity		ASTM D1003	7.0	%
gloss		ASTM2457	58
turbidity	25.4um	ASTM D-1003	7	%
gloss	45°，25.4um	ASTM D-2457	58
Other performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Film toughness	25.4um，TD	ASTM D-882	115	J/cm4
Film toughness	Film toughness	25.4um，MD	ASTM D-882	97.5	J/cm³
Thin film puncture strength	25.4um	Internal Method	7.69	J/cm³
Elmendorf tear strength		ASTM D1922	2.80	g/micron
Elmendorf tear strength	Elmendorf tear strength		ASTM D1922	16.3	g/micron
impact force		ASTM D882	1178	ft-lbf/in3
impact force	impact force		ASTM D882	1389	ft-lbf/in3
machinability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt Temperature			204-246	°C
Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	1	g/10min
density		ASTM D-792	0.935	g/m3
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact		ASTM D1709	112	g
Elmendorf tear strength		ASTM D192	413	g
	Elmendorf tear strength	25.4um，MD	ASTM D-1922	71	g
	Elmendorf tear strength	Elmendorf tear strength	25.4um，TD	ASTM D-1922	410	g
Dart impact	25.4um	ASTM D-1709A	110	g
Elongation at Break	25.4um，MD	ASTM D-882	520	%
Elongation at Break	Elongation at Break	25.4um，TD	ASTM D-882	660	%
tensile strength	25.4um，MD,Break	ASTM D-882	38.3	Mpa
	tensile strength	25.4um，TD,Break	ASTM D-882	33.1	Mpa
		tensile strength	25.4um，Yield,TD	ASTM D-882	16.7	Mpa
			tensile strength	25.4um，Yield,MD	ASTM D-882	15.2	Mpa
				tensile strength		ASTM D882	15.23	Mpa
				tensile strength	tensile strength		ASTM D882	16.72	Mpa
Secant modulus		ASTM D882	377.3	Mpa
Secant modulus	Secant modulus		ASTM D882	348.5	Mpa
tensile strength		ASTM D882	38.34	Mpa
tensile strength	tensile strength		ASTM D882	33.13	Mpa
impact force			93	ft-lbf/in3
elongation	Break	ASTM D882	522	%
elongation	elongation	Break	ASTM D882	656	%
Elmendorf tear strength		ASTM D192	71	g
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melting temperature		Internal Method	126	°C
Vicat softening temperature		ASTM D-1525	120	°C
	Vicat softening temperature		ASTM1525	120	°C
	Vicat softening temperature	Vicat softening temperature	Melting Temperature	陶氏化学方法(DSC	126	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	厚度		25.4	microns
melt mass-flow rate	melt mass-flow rate	℃/Kg	ASTM D1238	1.0	g/10min