TPU-Ester Texin® 255 Covestro - Polycarbonates

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD：2.54mm	ASTM D955	0.80 %
Shrinkage rate	Shrinkage rate	MD：2.54mm	ASTM D955	0.80 %
density		ASTM D792	1.21 g/cm³
density	density		ISO 1183	1.21 g/cm³
Shrinkage rate	TD:2.54mm	ISO 2577	0.80 %
Shrinkage rate	Shrinkage rate	MD:2.54mm	ISO 2577	0.80 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	邵氏D	ASTM D2240	55
Shore hardness	Shore hardness	邵氏D	ISO 868	55

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.5mm	UL 94	HB

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
CompressiveLoad	10%Deflection	ASTM D575	7.41 MPa
	CompressiveLoad	15%Deflection	ASTM D575	10.1 MPa
		CompressiveLoad	2%Deflection	ASTM D575	0.965 MPa
			CompressiveLoad	20%Deflection	ASTM D575	12.7 MPa
				CompressiveLoad	25%Deflection	ASTM D575	15.5 MPa
					CompressiveLoad	5%Deflection	ASTM D575	3.90 MPa
					CompressiveLoad	CompressiveLoad	50%Deflection	ASTM D575	40.6 MPa

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Taber abraser	1000Cycles,1000g,H-18转轮	ASTM D1044	50.0 mg
Flexural modulus	-30°C	ASTM D790	1210 MPa
	Flexural modulus	23°C	ASTM D790	68.9 MPa
		Flexural modulus	70°C	ASTM D790	51.7 MPa
			Flexural modulus	-30°C	ISO 178	1210 MPa
				Flexural modulus	23°C	ISO 178	68.9 MPa
				Flexural modulus	Flexural modulus	70°C	ISO 178	51.7 MPa
shear strength		ASTM D732	38.5 MPa
Taber abraser	1000Cycles,1000g,H-18转轮	ISO 4649	50.0 mg

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dart impact	-30°C,2.54mm,TotalEnergy	ASTM D3763	50.0 J
Dart impact	Dart impact	23°C,2.54mm,TotalEnergy	ASTM D3763	57.8 J

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	50%应变	ISO 37	12.4 MPa
tensile strength	tensile strength	50%应变	ASTM D412	12.4 MPa
compression set	70°C,22hr3	ASTM D395B	35 %
	compression set	70°C,22hr	ASTM D395B	65 %
		compression set	100°C,22hr3	ASTM D395B	50 %
			compression set	100°C,22hr	ISO 815	75 %
			compression set	compression set	100°C,22hr3	ISO 815	50 %
Shore hardness		ASTM D2632	40 %
compression set	23°C,22hr3	ASTM D395B	15 %
	compression set	23°C,22hr	ASTM D395B	20 %
		compression set	100°C,22hr	ASTM D395B	75 %
			compression set	23°C,22hr3	ISO 815	15 %
				compression set	23°C,22hr	ISO 815	20 %
					compression set	70°C,22hr3	ISO 815	35 %
					compression set	compression set	70°C,22hr	ISO 815	65 %
tear strength		ISO 34-1	160 kN/m
tensile strength	100%应变	ASTM D412	15.9 MPa
	tensile strength	100%应变	ISO 37	15.9 MPa
		tensile strength	300%应变	ASTM D412	32.4 MPa
			tensile strength	300%应变	ISO 37	32.4 MPa
				tensile strength	Yield	ASTM D412	63.4 MPa
				tensile strength	tensile strength	Yield	ISO 37	63.4 MPa
elongation	Break	ASTM D412	500 %
elongation	elongation	Break	ISO 37	500 %
tear strength		ASTM D624	158 kN/m

aging	شرایط آزمون	روش آزمون	نتیجه آزمون
Change rate of ultimate elongation in air	23°C,168hr,inReferenceFuelA(Isooctane)	ASTM D471	9.0 %
	Change rate of ultimate elongation in air	23°C,168hr,甲醇	ASTM D471	6.0 %
		Change rate of ultimate elongation in air	23°C,336hr,inReferenceFuelA(Isooctane)	ASTM D471	-4.0 %
			Change rate of ultimate elongation in air	23°C,336hr,inReferenceFuelC	ASTM D471	-2.0 %
				Change rate of ultimate elongation in air	23°C,504hr,inReferenceFuelA(Isooctane)	ASTM D471	-2.0 %
				Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	23°C,504hr,inReferenceFuelC	ASTM D471	-8.0 %
Shore hardness	ShoreD,23°C,504hr,inReferenceFuelA(Isooctane)	ISO 175	6.0
	Shore hardness	ShoreD,23°C,504hr,inReferenceFuelC	ISO 175	-8.0
		Shore hardness	ShoreD,100°C,70hr,inASTM#1Oil	ISO 175	2.0
		Shore hardness	Shore hardness	ShoreD,100°C,70hr,inASTM#3Oil	ISO 175	2.0
Change rate of ultimate elongation in air	100°C,504hr,inASTM#1Oil	ASTM D471	16 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,504hr,inASTM#3Oil	ASTM D471	20 %
volume change	23°C,336hr,inReferenceFuelC	ASTM D471	14 %
	volume change	100°C,504hr,inASTM#1Oil	ISO 175	-1.0 %
		volume change	100°C,504hr,inASTM#3Oil	ISO 175	4.0 %
			volume change	23°C,504hr,inReferenceFuelC	ASTM D471	14 %
				volume change	23°C,168hr,inReferenceFuelA	ISO 175	0.0 %
					volume change	23°C,168hr,甲醇	ISO 175	10 %
						volume change	23°C,336hr,inReferenceFuelA	ISO 175	0.0 %
							volume change	23°C,336hr,inReferenceFuelC	ISO 175	14 %
							volume change	volume change	23°C,504hr,inReferenceFuelA	ISO 175	0.0 %
Change rate of hardness (Shore) in the air	ShoreD,23°C,336hr,inReferenceFuelC	ASTM D471	-6.0
	Change rate of hardness (Shore) in the air	ShoreD,23°C,504hr,inReferenceFuelA(Isooctane)	ASTM D471	6.0
		Change rate of hardness (Shore) in the air	ShoreD,23°C,504hr,inReferenceFuelC	ASTM D471	-8.0
			Change rate of hardness (Shore) in the air	ShoreD,100°C,70hr,inASTM#1Oil	ASTM D471	2.0
				Change rate of hardness (Shore) in the air	ShoreD,100°C,70hr,inASTM#3Oil	ASTM D471	2.0
					Change rate of hardness (Shore) in the air	ShoreD,100°C,168hr,inASTM#1Oil	ASTM D471	1.0
						Change rate of hardness (Shore) in the air	ShoreD,100°C,336hr,inASTM#1Oil	ASTM D471	-2.0
							Change rate of hardness (Shore) in the air	ShoreD,100°C,504hr,inASTM#1Oil	ASTM D471	0.0
							Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreD,100°C,504hr,inASTM#3Oil	ASTM D471	-1.0
Change rate of tensile strength in air	100%Strain,100°C,504hr,inASTM#1Oil	ISO 175	15 %
Shore hardness	ShoreD,100°C,168hr,inASTM#1Oil	ISO 175	1.0
	Shore hardness	ShoreD,100°C,336hr,inASTM#1Oil	ISO 175	-2.0
		Shore hardness	ShoreD,100°C,504hr,inASTM#1Oil	ISO 175	0.0
		Shore hardness	Shore hardness	ShoreD,100°C,504hr,inASTM#3Oil	ISO 175	-1.0
volume change	23°C,70hr,inReferenceFuelA	ASTM D471	0.0 %
	volume change	23°C,70hr,甲醇	ASTM D471	6.0 %
		volume change	23°C,168hr,inReferenceFuelA	ASTM D471	0.0 %
			volume change	23°C,504hr,inReferenceFuelA	ASTM D471	0.0 %
				volume change	100°C,168hr,inASTM#1Oil	ISO 175	0.0 %
				volume change	volume change	100°C,336hr,inASTM#1Oil	ISO 175	-1.0 %
Change rate of ultimate elongation in air	100°C,70hr,在ASTM#1油中	ASTM D471	8.0 %
	Change rate of ultimate elongation in air	100°C,70hr,在ASTM#3油中	ASTM D471	6.0 %
		Change rate of ultimate elongation in air	100°C,168hr,inASTM#1Oil	ASTM D471	12 %
		Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,336hr,inASTM#1Oil	ASTM D471	24 %
Change rate of hardness (Shore) in the air	ShoreD,23°C,336hr,inReferenceFuelA(Isooctane)	ASTM D471	-1.0
Change rate of tensile strength in air	100%Strain,100°C,336hr,inASTM#1Oil	ISO 175	14 %
	Change rate of tensile strength in air	300%Strain,100°C,336hr,inASTM#1Oil	ISO 175	-9.0 %
	Change rate of tensile strength in air	Change rate of tensile strength in air	100°C,504hr,inASTM#1Oil	ISO 175	-29 %
Shore hardness	ShoreD,23°C,70hr,inReferenceFuelA(Isooctane)	ISO 175	-4.0
	Shore hardness	ShoreD,23°C,70hr,inReferenceFuelC	ISO 175	-7.0
		Shore hardness	ShoreD,23°C,168hr,inReferenceFuelA(Isooctane)	ISO 175	1.0
			Shore hardness	ShoreD,23°C,168hr,inReferenceFuelC	ISO 175	-4.0
				Shore hardness	ShoreD,23°C,336hr,inReferenceFuelA(Isooctane)	ISO 175	-1.0
				Shore hardness	Shore hardness	ShoreD,23°C,336hr,inReferenceFuelC	ISO 175	-6.0
Change rate of tensile strength in air	300%Strain,100°C,504hr,inASTM#1Oil	ISO 175	-14 %
	Change rate of tensile strength in air	100°C,504hr,inASTM#3Oil	ISO 175	-18 %
		Change rate of tensile strength in air	100%Strain,100°C,504hr,inASTM#3Oil	ISO 175	2.0 %
		Change rate of tensile strength in air	Change rate of tensile strength in air	300%Strain,100°C,504hr,inASTM#3Oil	ISO 175	-12 %
Change rate of ultimate elongation in air	23°C,70hr,inReferenceFuelA(Isooctane)	ASTM D471	-4.0 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	23°C,70hr,甲醇	ASTM D471	5.0 %
Tensile stress change rate	23°C,504hr,inReferenceFuelA(Isooctane)，断裂	ISO 175	-2.0 %
Tensile stress change rate	Tensile stress change rate	23°C,504hr,inReferenceFuelC，断裂	ISO 175	-8.0 %
Change rate of hardness (Shore) in the air	ShoreD,23°C,168hr,inReferenceFuelA(Isooctane)	ASTM D471	1.0
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreD,23°C,168hr,inReferenceFuelC	ASTM D471	-4.0
Change rate of tensile strength in air	300%Strain,100°C,70hr,inASTM#1Oil	ISO 175	7.0 %
	Change rate of tensile strength in air	23°C,70hr,甲醇	ISO 175	1.0 %
		Change rate of tensile strength in air	100%Strain,23°C,70hr,inReferenceFuelC	ISO 175	-19 %
			Change rate of tensile strength in air	300%Strain,23°C,70hr,inReferenceFuelC	ISO 175	-22 %
				Change rate of tensile strength in air	23°C,168hr,inReferenceFuelA(Isooctane)	ISO 175	-3.0 %
					Change rate of tensile strength in air	100%Strain,23°C,168hr,inReferenceFuelA(Isooctane)	ISO 175	-2.0 %
						Change rate of tensile strength in air	300%Strain,23°C,168hr,inReferenceFuelA(Isooctane)	ISO 175	-11 %
						Change rate of tensile strength in air	Change rate of tensile strength in air	23°C,168hr,甲醇	ISO 175	-4.0 %
Change rate of hardness (Shore) in the air	ShoreD,100°C,336hr	ISO 216	0.0
Change rate of tensile strength in air	300%Strain,23°C,70hr,inReferenceFuelA(Isooctane)	ASTM D471	5.0 %
	Change rate of tensile strength in air	300%Strain,23°C,70hr,inReferenceFuelC	ASTM D471	-22 %
	Change rate of tensile strength in air	Change rate of tensile strength in air	300%Strain125°C,168hr	ISO 216	-15 %
Change rate of ultimate elongation in air	125°C,504hr	ASTM D573	30 %
Tensile stress change rate	100°C,70hr，断裂	ISO 216	-3.0 %
Tensile stress change rate	Tensile stress change rate	100°C,168hr，断裂	ISO 216	7.0 %
Change rate of tensile strength in air	100°C,336hr	ASTM D573	14 %
	Change rate of tensile strength in air	100%Strain,100°C,336hr	ASTM D573	13 %
		Change rate of tensile strength in air	300%Strain,100°C,336hr	ASTM D573	-1.0 %
			Change rate of tensile strength in air	23°C,336hr,inReferenceFuelC	ASTM D471	-10 %
				Change rate of tensile strength in air	100%Strain,23°C,336hr,inReferenceFuelC	ASTM D471	-32 %
					Change rate of tensile strength in air	300%Strain,23°C,336hr,inReferenceFuelC	ASTM D471	-35 %
						Change rate of tensile strength in air	23°C,504hr,inReferenceFuelA(Isooctane)	ASTM D471	-1.0 %
							Change rate of tensile strength in air	100°C,336hr,inASTM#1Oil	ASTM D471	-20 %
								Change rate of tensile strength in air	100%Strain,100°C,336hr,inASTM#1Oil	ASTM D471	14 %
									Change rate of tensile strength in air	300%Strain,100°C,336hr,inASTM#1Oil	ASTM D471	-9.0 %
										Change rate of tensile strength in air	100°C,504hr,inASTM#1Oil	ASTM D471	-29 %
											Change rate of tensile strength in air	100%Strain,100°C,504hr,inASTM#1Oil	ASTM D471	15 %
												Change rate of tensile strength in air	300%Strain,100°C,504hr,inASTM#1Oil	ASTM D471	-14 %
													Change rate of tensile strength in air	100°C,504hr,inASTM#3Oil	ASTM D471	-18 %
														Change rate of tensile strength in air	100%Strain,100°C,504hr,inASTM#3Oil	ASTM D471	2.0 %
															Change rate of tensile strength in air	300%Strain,100°C,504hr,inASTM#3Oil	ASTM D471	-12 %
																Change rate of tensile strength in air	23°C,70hr,inReferenceFuelA(Isooctane)	ISO 175	6.0 %
																	Change rate of tensile strength in air	100%Strain,23°C,70hr,inReferenceFuelA(Isooctane)	ISO 175	2.0 %
																		Change rate of tensile strength in air	300%Strain,23°C,70hr,inReferenceFuelA(Isooctane)	ISO 175	5.0 %
																			Change rate of tensile strength in air	100%Strain,23°C,336hr,inReferenceFuelA(Isooctane)	ISO 175	3.0 %
																				Change rate of tensile strength in air	23°C,70hr,甲醇	ASTM D471	1.0 %
																					Change rate of tensile strength in air	100%Strain,23°C,70hr,inReferenceFuelC	ASTM D471	-19 %
																						Change rate of tensile strength in air	300%Strain100°C,504hr	ISO 216	1.0 %
																							Change rate of tensile strength in air	125°C,70hr	ISO 216	-20 %
																								Change rate of tensile strength in air	100%Strain125°C,70hr	ISO 216	7.0 %
																									Change rate of tensile strength in air	300%Strain125°C,70hr	ISO 216	-23 %
																										Change rate of tensile strength in air	125°C,168hr	ISO 216	-11 %
																										Change rate of tensile strength in air	Change rate of tensile strength in air	100%应变125°C,168hr	ISO 216	-2.0 %
Tensile stress change rate	100°C,336hr，断裂	ISO 216	14 %
	Tensile stress change rate	100°C,504hr，断裂	ISO 216	15 %
	Tensile stress change rate	Tensile stress change rate	125°C,70hr，断裂	ISO 216	28 %
Change rate of tensile strength in air	300%Strain100°C,70hr	ISO 216	1.0 %
	Change rate of tensile strength in air	100°C,168hr	ISO 216	8.0 %
		Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 216	4.0 %
			Change rate of tensile strength in air	300%Strain100°C,168hr	ISO 216	-5.0 %
				Change rate of tensile strength in air	100°C,336hr	ISO 216	14 %
					Change rate of tensile strength in air	100%Strain100°C,336hr	ISO 216	13 %
						Change rate of tensile strength in air	300%Strain100°C,336hr	ISO 216	-1.0 %
							Change rate of tensile strength in air	100°C,504hr	ISO 216	14 %
								Change rate of tensile strength in air	100%Strain100°C,504hr	ISO 216	14 %
									Change rate of tensile strength in air	125°C,504hr	ISO 216	-27 %
										Change rate of tensile strength in air	100%Strain125°C,504hr	ISO 216	4.0 %
										Change rate of tensile strength in air	Change rate of tensile strength in air	300%Strain125°C,504hr	ISO 216	-30 %
Change rate of ultimate elongation in air	100°C,70hr	ASTM D573	-3.0 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	7.0 %
volume change	23°C,168hr,甲醇	ASTM D471	10 %
	volume change	23°C,336hr,inReferenceFuelA	ASTM D471	0.0 %
		volume change	100°C,70hr,在ASTM#1油中	ASTM D471	-1.0 %
			volume change	100°C,70hr,在ASTM#3油中	ASTM D471	2.0 %
				volume change	100°C,168hr,inASTM#1Oil	ASTM D471	0.0 %
					volume change	100°C,336hr,inASTM#1Oil	ASTM D471	-1.0 %
						volume change	100°C,504hr,inASTM#1Oil	ASTM D471	-1.0 %
							volume change	100°C,504hr,inASTM#3Oil	ASTM D471	4.0 %
								volume change	23°C,70hr,inReferenceFuelA	ISO 175	0.0 %
									volume change	23°C,70hr,甲醇	ISO 175	6.0 %
										volume change	23°C,504hr,inReferenceFuelC	ISO 175	14 %
											volume change	100°C,70hr,在ASTM#1油中	ISO 175	-1.0 %
											volume change	volume change	100°C,70hr,在ASTM#3油中	ISO 175	2.0 %
Change rate of tensile strength in air	100°C,168hr	ASTM D573	8.0 %
Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	4.0 %
Tensile stress change rate	23°C,70hr,inReferenceFuelA(Isooctane)，断裂	ISO 175	-4.0 %
	Tensile stress change rate	23°C,70hr,甲醇，断裂	ISO 175	5.0 %
		Tensile stress change rate	23°C,168hr,inReferenceFuelA(Isooctane)，断裂	ISO 175	9.0 %
			Tensile stress change rate	23°C,168hr,甲醇，断裂	ISO 175	6.0 %
				Tensile stress change rate	23°C,336hr,inReferenceFuelA(Isooctane)，断裂	ISO 175	-4.0 %
				Tensile stress change rate	Tensile stress change rate	23°C,336hr,inReferenceFuelC，断裂	ISO 175	-2.0 %
Change rate of tensile strength in air	100°C,504hr	ASTM D573	14 %
	Change rate of tensile strength in air	100%Strain,100°C,504hr	ASTM D573	14 %
		Change rate of tensile strength in air	300%Strain,100°C,504hr	ASTM D573	1.0 %
			Change rate of tensile strength in air	125°C,70hr	ASTM D573	-20 %
				Change rate of tensile strength in air	100%Strain,125°C,70hr	ASTM D573	7.0 %
				Change rate of tensile strength in air	Change rate of tensile strength in air	300%Strain,125°C,70hr	ASTM D573	-23 %
Tensile stress change rate	100°C,70hr,在ASTM#1油中，断裂	ISO 175	8.0 %
	Tensile stress change rate	100°C,70hr,在ASTM#3油中，断裂	ISO 175	6.0 %
		Tensile stress change rate	100°C,168hr,inASTM#1Oil，断裂	ISO 175	12 %
			Tensile stress change rate	100°C,336hr,inASTM#1Oil，断裂	ISO 175	24 %
				Tensile stress change rate	100°C,504hr,inASTM#1Oil，断裂	ISO 175	16 %
				Tensile stress change rate	Tensile stress change rate	100°C,504hr,inASTM#3Oil，断裂	ISO 175	20 %
Change rate of hardness (Shore) in the air	ShoreD,23°C,70hr,inReferenceFuelA(Isooctane)	ASTM D471	-4.0
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreD,23°C,70hr,inReferenceFuelC	ASTM D471	-7.0
Change rate of tensile strength in air	300%Strain,100°C,168hr,inASTM#1Oil	ISO 175	2.0 %
	Change rate of tensile strength in air	100%Strain,23°C,504hr,inReferenceFuelA(Isooctane)	ASTM D471	5.0 %
		Change rate of tensile strength in air	300%Strain,23°C,504hr,inReferenceFuelA(Isooctane)	ASTM D471	3.0 %
			Change rate of tensile strength in air	23°C,504hr,inReferenceFuelC	ASTM D471	-11 %
				Change rate of tensile strength in air	100%Strain,23°C,504hr,inReferenceFuelC	ASTM D471	-27 %
					Change rate of tensile strength in air	300%Strain,23°C,504hr,inReferenceFuelC	ASTM D471	-28 %
						Change rate of tensile strength in air	100°C,70hr,在ASTM#1油中	ASTM D471	18 %
							Change rate of tensile strength in air	100%Strain,23°C,336hr,inReferenceFuelC	ISO 175	-32 %
								Change rate of tensile strength in air	300%Strain,23°C,336hr,inReferenceFuelC	ISO 175	-35 %
									Change rate of tensile strength in air	23°C,504hr,inReferenceFuelA(Isooctane)	ISO 175	-1.0 %
										Change rate of tensile strength in air	100%Strain,23°C,504hr,inReferenceFuelA(Isooctane)	ISO 175	5.0 %
											Change rate of tensile strength in air	300%Strain,23°C,504hr,inReferenceFuelA(Isooctane)	ISO 175	3.0 %
												Change rate of tensile strength in air	23°C,504hr,inReferenceFuelC	ISO 175	-11 %
													Change rate of tensile strength in air	100%Strain,23°C,504hr,inReferenceFuelC	ISO 175	-27 %
														Change rate of tensile strength in air	300%Strain,23°C,504hr,inReferenceFuelC	ISO 175	-28 %
															Change rate of tensile strength in air	100°C,70hr,在ASTM#1油中	ISO 175	18 %
																Change rate of tensile strength in air	100%Strain,100°C,70hr,inASTM#1Oil	ISO 175	12 %
																	Change rate of tensile strength in air	100%Strain,23°C,168hr,inReferenceFuelC	ISO 175	-27 %
																		Change rate of tensile strength in air	300%Strain,23°C,168hr,inReferenceFuelC	ISO 175	-34 %
																			Change rate of tensile strength in air	23°C,336hr,inReferenceFuelA(Isooctane)	ISO 175	6.0 %
																				Change rate of tensile strength in air	100%Strain,100°C,70hr,inASTM#1Oil	ASTM D471	12 %
																					Change rate of tensile strength in air	300%Strain,100°C,70hr,inASTM#1Oil	ASTM D471	7.0 %
																						Change rate of tensile strength in air	100°C,70hr,在ASTM#3油中	ASTM D471	19 %
																							Change rate of tensile strength in air	100%Strain,100°C,70hr,inASTM#3Oil	ASTM D471	16 %
																								Change rate of tensile strength in air	300%Strain,100°C,70hr,inASTM#3Oil	ASTM D471	13 %
																									Change rate of tensile strength in air	100°C,168hr,inASTM#1Oil	ASTM D471	-4.0 %
																										Change rate of tensile strength in air	100%Strain,100°C,168hr,inASTM#1Oil	ASTM D471	14 %
																											Change rate of tensile strength in air	300%Strain,100°C,168hr,inASTM#1Oil	ASTM D471	2.0 %
																												Change rate of tensile strength in air	23°C,168hr,inReferenceFuelA(Isooctane)	ASTM D471	-3.0 %
																													Change rate of tensile strength in air	100%Strain,23°C,168hr,inReferenceFuelA(Isooctane)	ASTM D471	-2.0 %
																														Change rate of tensile strength in air	300%Strain,23°C,168hr,inReferenceFuelA(Isooctane)	ASTM D471	-11 %
																															Change rate of tensile strength in air	100%Strain125°C,336hr	ISO 216	8.0 %
																															Change rate of tensile strength in air	Change rate of tensile strength in air	300%Strain125°C,336hr	ISO 216	-27 %
Change rate of hardness (Shore) in the air	ShoreD,100°C,168hr	ASTM D573	-1.0
	Change rate of hardness (Shore) in the air	ShoreD,100°C,336hr	ASTM D573	0.0
		Change rate of hardness (Shore) in the air	ShoreD,100°C,504hr	ASTM D573	0.0
			Change rate of hardness (Shore) in the air	ShoreD,125°C,70hr	ASTM D573	1.0
				Change rate of hardness (Shore) in the air	支撐D,125°C,168hr	ASTM D573	0.0
					Change rate of hardness (Shore) in the air	ShoreD,125°C,336hr	ASTM D573	-5.0
						Change rate of hardness (Shore) in the air	ShoreD,125°C,504hr	ASTM D573	-4.0
							Change rate of hardness (Shore) in the air	ShoreD,100°C,70hr	ISO 216	-2.0
							Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreD,100°C,168hr	ISO 216	-1.0
Change rate of tensile strength in air	125°C,168hr	ASTM D573	-11 %
	Change rate of tensile strength in air	100%Strain,125°C,168hr	ASTM D573	-2.0 %
		Change rate of tensile strength in air	300%Strain,125°C,168hr	ASTM D573	-15 %
			Change rate of tensile strength in air	125°C,336hr	ASTM D573	-23 %
				Change rate of tensile strength in air	100%Strain,125°C,336hr	ASTM D573	8.0 %
					Change rate of tensile strength in air	300%Strain,125°C,336hr	ASTM D573	-27 %
						Change rate of tensile strength in air	125°C,504hr	ASTM D573	-27 %
							Change rate of tensile strength in air	100%Strain,125°C,504hr	ASTM D573	4.0 %
								Change rate of tensile strength in air	300%Strain,125°C,504hr	ASTM D573	-30 %
								Change rate of tensile strength in air	Change rate of tensile strength in air	100°C,70hr	ISO 216	3.0 %
Tensile stress change rate	125°C,168hr，断裂	ISO 216	24 %
Change rate of ultimate elongation in air	100°C,336hr	ASTM D573	14 %
	Change rate of ultimate elongation in air	100°C,504hr	ASTM D573	15 %
		Change rate of ultimate elongation in air	125°C,70hr	ASTM D573	28 %
			Change rate of ultimate elongation in air	125°C,168hr	ASTM D573	24 %
			Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	125°C,336hr	ASTM D573	35 %
Change rate of hardness (Shore) in the air	ShoreD,100°C,504hr	ISO 216	0.0
	Change rate of hardness (Shore) in the air	ShoreD,125°C,70hr	ISO 216	1.0
		Change rate of hardness (Shore) in the air	支撐D,125°C,168hr	ISO 216	0.0
			Change rate of hardness (Shore) in the air	ShoreD,125°C,336hr	ISO 216	-5.0
			Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreD,125°C,504hr	ISO 216	-4.0
Change rate of tensile strength in air	23°C,70hr,inReferenceFuelA(Isooctane)	ASTM D471	6.0 %
	Change rate of tensile strength in air	100%Strain,23°C,70hr,inReferenceFuelA(Isooctane)	ASTM D471	2.0 %
		Change rate of tensile strength in air	100%Strain100°C,70hr	ISO 216	11 %
			Change rate of tensile strength in air	100°C,70hr	ASTM D573	3.0 %
				Change rate of tensile strength in air	100%Strain,100°C,70hr	ASTM D573	11 %
					Change rate of tensile strength in air	300%Strain,100°C,70hr	ASTM D573	1.0 %
						Change rate of tensile strength in air	300%Strain,100°C,168hr	ASTM D573	-5.0 %
							Change rate of tensile strength in air	100°C,70hr,在ASTM#3油中	ISO 175	19 %
								Change rate of tensile strength in air	100%Strain,100°C,70hr,inASTM#3Oil	ISO 175	16 %
									Change rate of tensile strength in air	300%Strain,100°C,70hr,inASTM#3Oil	ISO 175	13 %
										Change rate of tensile strength in air	100°C,168hr,inASTM#1Oil	ISO 175	-4.0 %
											Change rate of tensile strength in air	100%Strain,100°C,168hr,inASTM#1Oil	ISO 175	14 %
												Change rate of tensile strength in air	100°C,336hr,inASTM#1Oil	ISO 175	-20 %
													Change rate of tensile strength in air	300%Strain,23°C,336hr,inReferenceFuelA(Isooctane)	ISO 175	-1.0 %
														Change rate of tensile strength in air	23°C,336hr,inReferenceFuelC	ISO 175	-10 %
															Change rate of tensile strength in air	23°C,168hr,甲醇	ASTM D471	-4.0 %
																Change rate of tensile strength in air	100%Strain,23°C,168hr,inReferenceFuelC	ASTM D471	-27 %
																	Change rate of tensile strength in air	300%Strain,23°C,168hr,inReferenceFuelC	ASTM D471	-34 %
																		Change rate of tensile strength in air	23°C,336hr,inReferenceFuelA(Isooctane)	ASTM D471	6.0 %
																			Change rate of tensile strength in air	100%Strain,23°C,336hr,inReferenceFuelA(Isooctane)	ASTM D471	3.0 %
																				Change rate of tensile strength in air	300%Strain,23°C,336hr,inReferenceFuelA(Isooctane)	ASTM D471	-1.0 %
																				Change rate of tensile strength in air	Change rate of tensile strength in air	125°C,336hr	ISO 216	-23 %
Tensile stress change rate	125°C,336hr，断裂	ISO 216	35 %
Tensile stress change rate	Tensile stress change rate	125°C,504hr，断裂	ISO 216	30 %
Change rate of hardness (Shore) in the air	ShoreD,100°C,70hr	ASTM D573	-2.0

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	59.0 °C
Heat distortion temperature	Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	59.0 °C
brittle temperature		ASTM D746	<-68.0 °C
brittle temperature	brittle temperature		ISO 974	<-68.0 °C
Glass Transition Temperature		DMA	-26.0 °C
vicat		ASTM D15255	168 °C
vicat	vicat		ISO 306/50	168 °C
Linear coefficient of thermal expansion	MD	ASTM D696	1.3E-04 cm/cm/°C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.

تماس با ما

دریافت اپلیکیشن

Top