PA6 Latamid 6 H2 G/30-V0CT1 LATI S.p.A.

ویژگی‌ها:
Filler glass fiber reinforced material 30% filler by weight
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-20°C	ISO 179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of simply supported beam without notch	-20°C	ISO 179/1eU	35 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	800 °C
Hot filament ignition temperature	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	800 °C
Extreme Oxygen Index		ASTM D2863	28 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Break,23°C	ISO 527-2/5	125 MPa
	tensile strength	Break,60°C	ISO 527-2/5	80.0 MPa
		tensile strength	Break,90°C	ISO 527-2/5	60.0 MPa
			tensile strength	Break,120°C	ISO 527-2/5	50.0 MPa
			tensile strength	tensile strength	Break,150°C	ISO 527-2/5	40.0 MPa
Tensile strain	Break,23°C	ISO 527-2/5	2.0 %
	Tensile strain	Break,60°C	ISO 527-2/5	4.5 %
	Tensile strain	Tensile strain	Break,90°C	ISO 527-2/5	6.0 %
Tensile modulus	23°C	ISO 527-2/1	11000 MPa
	Tensile modulus	60°C	ISO 527-2/1	7400 MPa
		Tensile modulus	90°C	ISO 527-2/1	5100 MPa
			Tensile modulus	120°C	ISO 527-2/1	4200 MPa
			Tensile modulus	Tensile modulus	150°C	ISO 527-2/1	3600 MPa
Tensile strain	Break,120°C	ISO 527-2/5	7.0 %
Tensile strain	Tensile strain	Break,150°C	ISO 527-2/5	7.5 %

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	185 °C
Continuous use temperature			115 °C
Vicat softening temperature		ISO 306/B50	195 °C
Linear coefficient of thermal expansion	MD：30to100°C	ISO 11359-2	1.5E-05 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD:2.00mm	ISO 294-4	0.50to0.70 %
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	0.25to0.45 %
Water absorption rate	23°C,24hr	ISO 62	0.30 %
density		ISO 1183	1.54 g/cm³

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
dimensional stability			60.0