برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.90to2.10 g/cm³ |
| Apparent density | | ISO 60 | 0.75to0.90 g/cm³ |
| Shrinkage rate | MD：--2 | ISO 2577 | 0.30to0.40 % |
| Shrinkage rate | MD：--3 | ISO 2577 | 0.50to0.60 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.20 % |
| Shrinkage rate | | ISO 2577 | <0.050 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 930 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | Compression Molded | ISO 178 | 8000to12000 MPa |
| Flexural modulus | Injection | ISO 178 | 13000to16000 MPa |
| bending strength | Compression Molded | ISO 178 | 80.0to100 MPa |
| bending strength | Injection | ISO 178 | 100to140 MPa |
| compression stress | | ISO 604 | 150to200 MPa |
| tensile strength | CompressionMolded | ISO 527-2 | 35.0to60.0 MPa |
| tensile strength | Injection | ISO 527-2 | 40.0to70.0 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 6000to9000 MPa |
| Tensile modulus | Injection | ISO 527-2 | 9000to11000 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 2.5to3.5 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 3.5to5.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 5.0to10 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 8.0to11 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| arc resistance | | ASTM D495 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35to40 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 4.505.00 |
| relative permittivity | 1MHz | IEC 60250 | 4.004.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010to0.030 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010to0.030 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | >180 °C |
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 5.0E-6到1.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.90to1.1 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.