PA66 Vydyne® R540H

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density	23°C	ISO 1183	1.46 g/cm³
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.40 %
Water absorption rate	23°C,24hr	ISO 62	0.60 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	1.5 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	725 °C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	725 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	750 °C
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	0.75mm	IEC 60695-2-12	700 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	700 °C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	875 °C

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
Automotive Materials	thicknessd=1mm	FMVSS302	+

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength	23°C	ISO 178	335 MPa
Poisson's ratio		ISO 527	0.40
Flexural modulus	23°C	ISO 178	12300 MPa
Tensile modulus	23°C	ISO 527-2	14100 MPa
tensile strength	断裂,23°C	ISO 527-2	220 MPa
Tensile strain	断裂,23°C	ISO 527-2	3.0 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	12 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	90 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180	13 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	14 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	3.00mm	IEC 60093	1E+13 ohms·cm
dielectric strength	1.00mm	IEC 60243	20 kV/mm
arc resistance	3.00mm	ASTM D495	PLC6
Compared to the Leakage Tracking Index (CTI)	3.00mm	IEC 60112	PLC 2
High arc combustion index (HAI)	0.75mm	UL 746	PLC 0
	High arc combustion index (HAI)	1.5mm	UL 746	PLC 0
	High arc combustion index (HAI)	High arc combustion index (HAI)	3.0mm	UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)	HVTR	UL 746	PLC 1
Hot wire ignition (HWI)	0.75mm	UL 746	PLC 4
	Hot wire ignition (HWI)	1.5mm	UL 746	PLC 3
	Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0mm	UL 746	PLC 4

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
RTI Imp	1.5mm	UL 746	125 °C
RTI Imp	RTI Imp	3.0mm	UL 746	125 °C
RTI Str	0.75mm	UL 746	140 °C
Hot deformation temperature (HDT)	0.45MPa,未退火，HDT	ISO 75-2/B	260 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)	1.8MPa,未退火，HDT	ISO 75-2/A	252 °C
melting temperature		ISO 11357-3	260 °C
线性热膨胀系数	MD：23to55°C,2.00mm	ISO 11359-2	1.7E-05 cm/cm/°C
线性热膨胀系数	线性热膨胀系数	TD：23to55°C,2.00mm	ISO 11359-2	1E-04 cm/cm/°C
RTI Elec	0.75mm	UL 746	140 °C
RTI Str	1.5mm	UL 746	140 °C
RTI Str	RTI Str	3.0mm	UL 746	140 °C
RTI Elec	1.5mm	UL 746	140 °C
RTI Elec	RTI Elec	3.0mm	UL 746	140 °C
RTI Imp	0.75mm	UL 746	125 °C