PA66 NILAMID® A3 W GF30 Celanese Corporation

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.34 g/cm³
Shrinkage rate	MD	ISO 294-4	0.40 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.20 %
Water absorption rate	(23°C,24hr)	ISO 62	1.80 %
Water absorption rate	Water absorption rate	(23°C,50RH)	ISO 62	6.00 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	N/D kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	N/D kJ/m²
tensile strength	23°C	ISO 527-2	185 MPa
elongation at break	23°C	ISO 527-2	3.5 %
Tensile modulus	23°C	ISO 527-2	9200 MPa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.0 kJ/m²

Flame retardant performance	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating		UL -94	HB 1.50mm
UL flame retardant rating	UL flame retardant rating		UL -94	HB 3.00mm
Limiting Oxygen Index		ISO 4589-2	28 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		IEC 60093	1E+15 Ω.cm
Dissipation Factor	相对漏电起痕指数	IEC 60112	550 V

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa未退火，HDT	ISO 75-2/Bf	250 °C
Heat distortion temperature	Heat distortion temperature	1.80MPa退火，HDT	ISO 75-2/Af	250 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.