برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.19 g/cm³ |
| Apparent density | | ASTM D1895 | 0.66 g/cm³ |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 7.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| Water absorption rate | Equilibrium | ASTM D570 | <0.30 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 94 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Yellowness Index | 3.20mm | ASTM D1925 | <1.0 YI |
| transmissivity | 3200µm | ASTM D1003 | 92.0 % |
| Haze ratio | 3200µm | ASTM D1003 | <1.0 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 3240 MPa |
| tensile strength | | ASTM D638 | 65.5 MPa |
| elongation | Yield | ASTM D638 | 4.0to6.0 % |
| elongation | Break | ASTM D638 | 4.0to6.0 % |
| Flexural modulus | | ASTM D790 | 3380 MPa |
| bending strength | | ASTM D790 | 117 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 19 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,退火,6.35mm，HDT | ASTM D648 | 93.9 °C |
| vicat | | ASTM D1525 | 105 °C |
| Linear coefficient of thermal expansion | MD：0到156°C | ASTM D696 | 7.2E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.