physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.5 g/10min |
optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
gloss | 45°,25.4um | ASTM D-2457 | 90 |
Haze ratio | 25.4um | ASTM D-1003 | 2.6 % |
gloss | 45°,25.4µm | ASTM D2457 | 90 |
Haze ratio | 25.4µm | ASTM D1003 | 2.6 % |
processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Melt Temperature | | | 274 °C |
Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | | ASTM D-792 | 0.935 g/m3 |
melt mass-flow rate | | ASTM D-1238 | 2.5 g/10min |
film thickness | | | 25.4 um |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tensile strength | 25.4um,屈服,MD | ASTM D-882 | 17.6 Mpa |
tensile strength | 25.4um,屈服,MD | ASTM D-882 | 16.9 Mpa |
tensile strength | 25.4um,TD,断裂 | ASTM D-882 | 39.9 Mpa |
tensile strength | 25.4um,MD,断裂 | ASTM D-882 | 59.2 Mpa |
elongation at break | 25.4um,MD | ASTM D-882 | 620 % |
elongation at break | 25.4um,TD | ASTM D-882 | 750 % |
Dart impact | 25.4um | ASTM D-1709A | 57 g |
Elmendorf tear strength | 25.4um,MD | ASTM D-1922 | 83 g |
Elmendorf tear strength | 25.4um,TD | ASTM D-1922 | 290 g |
Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Thin film puncture strength | 25.4um | 内部方法 | 10.3 J/cm³ |
Film toughness | 25.4um,MD | ASTM D-882 | 324 J/cm³ |
Film toughness | 25.4um,TD | ASTM D-882 | 308 J/cm4 |
film | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
elongation | MD:断裂,25µm | ASTM D882 | 620 % |
elongation | TD:断裂,25µm | ASTM D882 | 750 % |
Dart impact | 25µm | ASTM D1709A | 57 g |
Elmendorf tear strength | MD:25µm | ASTM D1922 | 83 g |
Elmendorf tear strength | TD:25µm | ASTM D1922 | 290 g |
film thickness | | | 25 µm |
Thin film puncture strength | 25µm | 内部方法 | 10.3 J/cm³ |
film strength | MD:25µm | ASTM D882 | 324 J/cm³ |
film strength | TD:25µm | ASTM D882 | 308 J/cm³ |
tensile strength | MD:屈服,25µm | ASTM D882 | 16.9 Mpa |
tensile strength | TD:屈服,25µm | ASTM D882 | 17.6 Mpa |
tensile strength | MD:断裂,25µm | ASTM D882 | 59.2 Mpa |
tensile strength | TD:断裂,25µm | ASTM D882 | 39.9 Mpa |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
vicat | | ASTM D-1525 | 119 °C |
melting temperature | | 内部方法 | 125 °C |
vicat | | ASTM D1525 | 119 °C |
melting temperature | | 内部方法 | 125 °C |