PA LNP™ THERMOTUF™ V1000SU compound SABIC

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	23°C,TotalEnergy	ASTM D3763	49.8	J
Multi axis Instrumented Impact Energy		ISO 6603-2	49.4	J
Impact strength of cantilever beam gap	23°C	ASTM D256	200	J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	27	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	NoBreak
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ASTM D638	1710	MPa
Tensile modulus	Tensile modulus		ISO 527-2/1	1650	MPa
tensile strength	Yield	ASTM D638	39.0	MPa
	tensile strength	Yield	ISO 527-2/5	41.0	MPa
		tensile strength	Break	ASTM D638	39.0	MPa
		tensile strength	tensile strength	Break	ISO 527-2/5	41.0	MPa
elongation	Yield	ASTM D638	57	%
Tensile strain	Yield	ISO 527-2/5	150	%
elongation	Break	ASTM D638	85	%
Tensile strain	Break	ISO 527-2/5	170	%
Bending modulus		ASTM D790	2070	MPa
Bending modulus	Bending modulus		ISO 178	1700	MPa
bending strength		ASTM D790	55.2	MPa
bending strength	bending strength		ISO 178	53.0	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	192	°C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	150	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	193	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	147	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.4E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	1.3E-04	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.3E-04	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.3E-04	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D792	1.071.08	g/cm³
	density		ASTM D792	1.07	g/cm³
	density	density		ISO 1183	1.08	g/cm³
Shrinkage rate	MD：24hr	ASTM D955	2.1to2.3	%
	Shrinkage rate	TD：24hr	ASTM D955	2.5to2.7	%
		Shrinkage rate	TD:24hr	ISO 294-4	2.6	%
		Shrinkage rate	Shrinkage rate	MD:24hr	ISO 294-4	2.2	%
Water absorption rate	24hr,50%RH	ASTM D570	0.60	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.0	%