| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 0.934 g/cm³ |
| Apparent density | | ASTM D1895 | 0.34 g/cm³ |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 5.0 g/10min |
| Environmental stress cracking resistance | 100%Igepal,RotationalMolded,F50 | ASTM D1693B | 1000 hr |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Pourability | | ASTM D1895 | 30.0 sec |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield,RotationalMolded | ASTM D638 | 19.3 MPa |
| Tensile strain | Break,RotationalMolded | ASTM D638 | 400 % |
| Flexural modulus | RotationalMolded，正切 | ASTM D790 | 793 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -40°C,RotationalMolded | ARM | 92 J |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火,滚塑成形，HDT | ASTM D648 | 63.0 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,RotationalMolded，HDT | ASTM D648 | 42.0 °C |