PS Generic PPE+PS+Nylon Generic

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	23°C	ASTM D3763	4.00to60.0	J
Impact strength of cantilever beam gap	23°C	ISO 180	9.5to55	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	73to680	J/m
Charpy Notched Impact Strength	23°C	ISO 179	11to55	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Break,23°C	ISO 527-2	45.0to55.5	MPa
bending strength	Yield,23°C	ASTM D790	74.7to99.3	MPa
	bending strength	23°C	ISO 178	70.0to103	MPa
	bending strength	bending strength	23°C	ASTM D790	73.5to85.7	MPa
Bending modulus	23°C	ISO 178	1860to2850	MPa
Bending modulus	Bending modulus	23°C	ASTM D790	1840to2730	MPa
elongation	Break,23°C	ISO 527-2	2.8to51	%
	elongation	Break,23°C	ASTM D638	2.2to100	%
		elongation	Yield,23°C	ISO 527-2	3.5to5.1	%
		elongation	elongation	Yield,23°C	ASTM D638	4.7to5.0	%
tensile strength	Break,23°C	ASTM D638	49.8to60.2	MPa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	50.0to65.2	MPa
Tensile modulus	23°C	ASTM D638	1820to3320	MPa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	2000to3050	MPa
tensile strength	Yield,23°C	ASTM D638	53.5to65.6	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	83.9to197	°C
Vicat softening temperature	--	ASTM D1525	178to233	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	174to193	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	154to196	°C
thermal conductivity	23°C	ISO 8302	0.23to0.24	W/m/K
Linear coefficient of thermal expansion	TD	ISO 11359-2	8.9E-5到9.1E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ASTME831	5.9E-5到1.0E-4	cm/cm/°C
Vicat softening temperature	--	ISO 306	169to246	°C
Linear coefficient of thermal expansion	MD	ASTME831	7.5E-5到9.8E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	8.0E-5到1.0E-4	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density	--	ASTM D792	1.07to1.12	g/cm³
density	density	23°C	ISO 1183	1.07to1.25	g/cm³
melt mass-flow rate	280°C/5.0kg	ASTM D1238	8.0to21	g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	7.50to19.0	cm³/10min
Shrinkage rate	MD:23°C	ASTM D955	1.2to1.8	%
Shrinkage rate	Shrinkage rate	TD:23°C	ASTM D955	1.1to1.3	%
Water absorption rate	23°C,24hr	ASTM D570	0.39to0.60	%
	Water absorption rate	Saturation,23°C	ISO 62	3.5to4.2	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dissipation factor	23°C	IEC 60250	0.024to0.072
Relative permittivity	23°C	IEC 60250	3.17
Volume resistivity	23°C	ASTM D257	4.0E+3到1.1E+15	ohms·cm
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	75.0to90.0	MPa