PPO(PPE)+PS+PP Generic PPE+PS+PP Generic

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ASTM D256	150to590 J/m
Dart impact	23°C	ASTM D3763	36.2to45.9 J

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield,23°C	ISO 527-2	33.9to44.6 MPa
tensile strength	tensile strength	Break,23°C	ASTM D638	27.6to41.5 MPa
elongation	Yield,23°C	ASTM D638	6.5to15 %
	elongation	Break,23°C	ASTM D638	83to200 %
	elongation	elongation	Break,23°C	ISO 527-2	46to120 %
Bending modulus	23°C	ASTM D790	1340to1560 MPa
bending strength	Yield,23°C	ASTM D790	49.0to53.2 MPa
Tensile modulus	23°C	ASTM D638	1170to1710 MPa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	1660to1760 MPa
tensile strength	Yield,23°C	ASTM D638	33.8to43.8 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	110to113 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	71.1to92.0 °C
Vicat softening temperature	--	ASTM D1525	85.0to146 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306	102to118 °C
Linear coefficient of thermal expansion	MD	ASTME831	8.1E-5到1.6E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ASTME831	7.2E-5到1.1E-4 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	0.987to1.03 g/cm³
melt mass-flow rate	260°C/5.0kg	ASTM D1238	11to16 g/10min
Shrinkage rate	MD：23°C	ASTM D955	0.65to1.0 %

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.