mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Yield，5mm/min，23°C	ASTM D638	46.0	Mpa
tensile strength	tensile strength	5mm/min，23°C	ASTM D638	47.0	Mpa
Elongation at Break	Yield，5mm/min，23°C	ASTM D638	4.2	%
Elongation at Break	Elongation at Break	5mm/min，23°C	ASTM D638	100	%
Tensile modulus	50mm/min，23°C	ASTM D638	2480	Mpa
bending strength	Yield，1.3mm/min，23°C	ASTM D790	80.0	Mpa
bending strength	bending strength	1.3mm/min，23°C	ASTM D790	79.0	Mpa
Bending modulus	1.3mm/min，23°C	ASTM D790	2400	Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	600	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	悬壁梁Unnotched冲击强度	ASTM D4812	NB	J/m
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	1.80MPaUnannealed	ASTM D648	108	°C
Linear coefficient of thermal expansion	MD	ASTM D696	8.47E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ASTM D696	9.1E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD3.20mm	ASTM D995	0.60-0.65	%
Shrinkage rate	Shrinkage rate	TD3.20mm	ASTM D995	0.50-0.56	%
Water absorption rate	(23°C,24hr)	ASTM D570	0.010	%
Water absorption rate	Water absorption rate	吸湿性	ASTM D570	0.0200	%