PC LEXAN™ 121R-111 SABIC INNOVATIVE SAUDI
39
- ویژگی‌ها:چسبندگی پایینعقب نشینیشفافیتمقاومت در برابر دمای بالا
- کاربردها:پروفایلمواد ساختمانیکاربردهای خودرو
مقایسه
مشاهده قیمتهابرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.20 g/cm³ | |
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| density | ASTM D792 | 1.19 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 18 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| 平衡,23°C | ASTM D570 | 0.35 % | |
| 平衡,100°C | ASTM D570 | 0.58 % | |
| Outdoor applicability | UL 746C | f2 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| R计秤 | ASTM D785 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | 0.70mm | UL 94 | HB |
| Radiation board grade | UL | YES |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 130 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 96.5 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| tensile strength | 屈服 | ASTM D638 | 62.1 Mpa |
| 断裂 | ASTM D638 | 68.9 Mpa | |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| 23°C | ISO 179/1eA | 65 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 690 J/m |
| -30°C | ISO 180/1A | 11 kJ/m² | |
| 23°C | ISO 180/1A | 65 kJ/m² | |
| 23°C | ASTM D4812 | 3200 J/m | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| 23°C | ISO 180/1U | NoBreak | |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 62.1 J |
| 23°C | ASTM D3029 | 169 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.17 |
| 60Hz | ASTM D150 | 3.17 | |
| 1MHz | ASTM D150 | 2.96 | |
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| 60Hz | ASTM D150 | 9E-04 | |
| 1MHz | ASTM D150 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 129 °C | |
| vicat | ASTM D15257 | 154 °C | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.25 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C |