ABS HU-600
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.04 23/23℃ | |
| melt mass-flow rate | 200℃ 21.6kg | ASTM D-1238 | 7 g/10min |
| Shrinkage rate | ASTM D-955 | 0.4-0.7 % | |
| melt mass-flow rate | 200℃ 5kg(条件G) | ASTM D-1238 | 1.7 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Flexural modulus | 23℃ | ASTM D-790 | 22000 kg/cm |
| bending strength | 23℃ | ASTM D-790 | 700 kg/cm |
| Impact strength of cantilever beam gap | 1/4in(6.4mm) 23℃ | ASTM D-256 | 14 kg.cm/cm |
| Rockwell hardness | ASTM D-785 | 108 R | |
| elongation | ASTM D-638 | 30 % | |
| tensile strength | 23℃ | ASTM D-638 | 510 kg/cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | ASTM D-1525 | 123(253) ℃(℉) | |
| Heat distortion temperature | 未退火，6.4mm 18.6kg/cm，HDT | ASTM D-648 | 102(216) ℃(℉) |
| 退火，6.4mm 18.6kg/cm，HDT | ASTM D-648 | 114(237) ℃(℉) |